- 密度 [g/cm3]: 1.52
- 彎曲強度 [MPa]: 140.0
- 彎曲模量 [MPa]: 8.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in3 | ISO 1183 | ||
| Viscosity Test | 92 cm3/g | 92 cm3/g | Viscosity number | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 140 MPa | 20300 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.2 % | 3.2 % | 5mm/min; ISO 527 | ||
| Flexural Strength | 212 MPa | 30700 psi | ISO Data | ||
| Flexural Modulus | 8.00 GPa | 1160 ksi | ISO Data | ||
| Charpy Impact Unnotched | 7.40 J/cm2 | 35.2 ft-lb/in2 | ISO 179 | ||
| Charpy Impact, Notched | 1.10 J/cm2 | 5.24 ft-lb/in2 | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 223 °C | 433 °F | 10 K/min | ||
| 223 °C | 433 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | BK15116 | ||||
| Commercial Status | North America and Europe | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||