- 密度 [g/cm3]: 1.23
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in3 | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | similar to ISO 62 test | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 40.0 MPa | 5800 psi | ISO 527-1 | ||
| Elongation at Break | 50 % | 50 % | ISO 527-1 | ||
| Tensile Modulus | 1.80 GPa | 261 ksi | ISO 527-1 | ||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179-1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179-1eU | |||
| Charpy Impact, Notched | 5.00 J/cm2 | 23.8 ft-lb/in2 | ISO 179-1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Strength | 26.0 kV/mm | 660 kV/in | IEC 60243-1 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Resin Type | PBT-I | ||||