- 熔體流動速率 [g/10min]: 20.0
- 密度 [g/cm3]: 1.29
- 熱變形溫度 [℃]: 155.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in3 | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | similar to ISO 62 test | ||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 235 °C | 20 g/10 min @Load 4.76 lb, Temperature 455 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | ISO 527-1 | ||
| Elongation at Break | >= 25 % | >= 25 % | ISO 527-1 | ||
| Elongation at Yield | 3.5 % | 3.5 % | ISO 527-1 | ||
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527-1 | ||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179-1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179-1eU | |||
| Charpy Impact, Notched | 0.600 J/cm2 | 2.86 ft-lb/in2 | ISO 179-1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Resin Type | PBT | ||||