Bayer MaterialScience Makroblend? S 7916 Polycarbonate + PBT, Impact Grade

Bayer MaterialScience Makroblend? S 7916 Polycarbonate + PBT, Impact Grade 物性表: Bayer MaterialScience Makroblend? S 7916 Polycarbonate + PBT, Impact Grade物性表及特性介紹,Bayer MaterialScience Makroblend? S 7916 Polycarbonate + PBT, Impact Grade注塑參數詳情,如需Bayer MaterialScience Makroblend? S 7916 Polycarbonate + PBT, Impact Grade下載, 可到相關下載區下載

熔體流動速率 [g/10min]: 13.0
密度 [g/cm3]: 1.2
吸水率 [%]: 0.5
拉伸強度 [MPa]: 40.0
熱變形溫度 [℃]: 110.0

Physical Properties	Metric	English	Comments

Density	1.20 g/cc	0.0434 lb/in3	ISO 1183
	1.02 g/cc @Temperature 260 °C	0.0368 lb/in3 @Temperature 500 °F	Melt
Water Absorption	0.50 %	0.50 %	Similar to ISO 62
Moisture Absorption at Equilibrium	0.20 %	0.20 %	Similar to ISO 62
Melt Flow	13 g/10 min @Load 5.00 kg, Temperature 260 °C	13 g/10 min @Load 11.0 lb, Temperature 500 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	40.0 MPa	5800 psi	ISO 527-1/-2
Elongation at Break	>= 50 %	>= 50 %	Nominal; ISO 527-1/-2
Elongation at Yield	4.0 %	4.0 %	ISO 527-1/-2
Tensile Modulus	1.80 GPa	261 ksi	ISO 527-1/-2
Charpy Impact Unnotched	NB	NB	ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179/1eU
Charpy Impact, Notched	6.90 J/cm2	32.8 ft-lb/in2	ISO 179/1eA
Tensile Creep Modulus, 1 hour	1500 MPa	218000 psi	ISO 899-1
Tensile Creep Modulus, 1000 hours	1200 MPa	174000 psi	ISO 899-1

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	IEC 60093
Dielectric Constant	2.9 @Frequency 1.00e+6 Hz	2.9 @Frequency 1.00e+6 Hz	IEC 60250
	3.1 @Frequency 100 Hz	3.1 @Frequency 100 Hz	IEC 60250
Dissipation Factor	0.0023 @Frequency 100 Hz	0.0023 @Frequency 100 Hz	IEC 60250
	0.014 @Frequency 1.00e+6 Hz	0.014 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	IEC 60112

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	110 μm/m-°C	61.1 μin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	110 μm/m-°C	61.1 μin/in-°F	ISO 11359-1/-2
Specific Heat Capacity	1.88 J/g-°C	0.449 BTU/lb-°F	Melt
Thermal Conductivity	0.185 W/m-K	1.28 BTU-in/hr-ft2-°F	Melt
Deflection Temperature at 0.46 MPa (66 psi)	110 °C	230 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	60.0 °C	140 °F	ISO 75-1/-2
Vicat Softening Point	119 °C	246 °F	50°C/h 50N; ISO 306
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in	IEC 60695-11-10
	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in	IEC 60695-11-10
Oxygen Index	20 %	20 %	ISO 4589-1/-2

Processing Properties	Metric	English	Comments
Melt Temperature	250 - 270 °C	482 - 518 °F
	260 °C	500 °F	Injection Molding; ISO 294
Mold Temperature	60.0 - 80.0 °C	140 - 176 °F
	70.0 °C	158 °F	Injection Molding; ISO 10724
Ejection Temperature	170 °C	338 °F
Injection Velocity	200 mm/sec	7.87 in/sec	ISO 294

Descriptive Properties
Availability	Asia Pacific
	Europe
	India
	Near East/Africa
	North America
	South and Central America
Eff. thermal diffusivity (m2/s)	9.6E-08
Feature	Release agent
Form	Pellets
Process	Injection Molding

關鍵詞:
PBT
供應
Impact Grade
Bayer MaterialScience Makroblend? S 7916 Polycarbonate + PBT

轉載請注明: 轉自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/yuanliaoku/show-37851.html

免責聲明: 本文 Bayer MaterialScience Makroblend? S 7916 Polycarbonate + PBT, Impact Grade 僅代表作者個人觀點，中國塑膠原料之家無關。中國塑膠原料之家網所轉載的內容，其版權均由原作者和資料提供方所擁有！如因作品版權問題需要處理，請與我們聯絡