- 熔體流動速率 [g/10min]: 10.4
- 密度 [g/cm3]: 1.73
- 吸水率 [%]: 0.4
- 熱變形溫度 [℃]: 221.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.73 g/cc | 0.0625 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.12 % | 0.12 % | 23°C/50% R.H. | ||
| Viscosity Test | 90 cm3/g | 90 cm3/g | Viscosity number | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | Sheet | ||
| 0.0024 cm/cm | 0.0024 in/in | 60x60x2mm; ISO 294 | |||
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | Sheet | ||
| 0.0077 cm/cm | 0.0077 in/in | 60x60x2mm; ISO 294 | |||
| Melt Flow | 10.4 g/10 min @Load 2.16 kg, Temperature 275 °C | 10.4 g/10 min @Load 4.76 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 165 MPa | 23900 psi | 5mm/min; ISO 527-2 | ||
| Elongation at Break | 1.5 % | 1.5 % | 5mm/min; ISO 527-2 | ||
| Modulus of Elasticity | 18.7 GPa | 2710 ksi | ISO 527-2 | ||
| Charpy Impact Unnotched | 5.20 J/cm2 | 24.7 ft-lb/in2 | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.00 J/cm2 | 4.76 ft-lb/in2 | ISO 179/1eA | ||
| Dart Drop, Total Energy | <= 5.00 J | <= 3.69 ft-lb | ISO 6603-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | IEC 60093 | ||
| Dielectric Constant | 4.5 @Frequency 1.00e+6 Hz | 4.5 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.7 @Frequency 100 Hz | 4.7 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | IEC 243/1 | ||
| Dissipation Factor | 0.015 @Frequency 1.00e+6 Hz | 0.015 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 0.020 @Frequency 100 Hz | 0.020 @Frequency 100 Hz | IEC 60250 | |||
| Comparative Tracking Index | 225 V | 225 V | Test solution A; IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 2.00 - 3.00 μm/m-°C @Temperature 23.0 - 80.0 °C | 1.11 - 1.67 μin/in-°F @Temperature 73.4 - 176 °F | DIN 53752 | ||
| Specific Heat Capacity | 1.60 J/g-°C | 0.382 BTU/lb-°F | IEC 1006 | ||
| Melting Point | 220 - 250 °C | 428 - 482 °F | |||
| Maximum Service Temperature, Air | 140 °C | 284 °F | at 50% loss of tensile strength after 20000h; IEC 216-1 | ||
| 160 °C | 320 °F | at 50% loss of tensile strength after 5000h; IEC 216-1 | |||
| 210 °C | 410 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection molding | ||
| 270 °C | 518 °F | for shrinkage test | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| 80.0 °C | 176 °F | for shrinkage test | |||
| Descriptive Properties | |||||
| Color | BK5110 and Colored | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Release agent | ||||