- 熔體流動速率 [g/10min]: 52.0
- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.5
- 拉伸強度 [MPa]: 57.0
- 熱變形溫度 [℃]: 165.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.50 % | 0.50 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.25 % | 0.25 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Test | 107 cm3/g | 107 cm3/g | Viscosity number | ||
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | |||
| 0.016 cm/cm | 0.016 in/in | 60x60x2mm; ISO 294 | |||
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | |||
| 0.019 cm/cm | 0.019 in/in | 60x60x2mm; ISO 294 | |||
| Melt Flow | 52 g/10 min @Load 2.16 kg, Temperature 250 °C | 52 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 130 MPa | 18900 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 57.0 MPa | 8270 psi | 5mm/min; ISO 527-2 | ||
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Break | 35 % | 35 % | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 3.7 % | 3.7 % | 50mm/min; ISO 527-2 | ||
| Modulus of Elasticity | 2.50 GPa | 363 ksi | ISO 527-2 | ||
| Charpy Impact Unnotched | 25.0 J/cm2 | 119 ft-lb/in2 | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.600 J/cm2 | 2.86 ft-lb/in2 | ISO 179/1eA | ||
| Dart Drop, Total Energy | 100 J | 73.8 ft-lb | ISO 6603-1 | ||
| Tensile Creep Modulus, 1000 hours | 1100 MPa | 160000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 93 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 93 | ||
| Dielectric Constant | 3.3 @Frequency 100 Hz | 3.3 @Frequency 100 Hz | IEC 250 | ||
| 3.3 @Frequency 1.00e+6 Hz | 3.3 @Frequency 1.00e+6 Hz | IEC 250 | |||
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 243/1 | ||
| Dissipation Factor | 0.0013 @Frequency 100 Hz | 0.0013 @Frequency 100 Hz | IEC 250 | ||
| 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 250 | |||
| Comparative Tracking Index | 450 V | 450 V | Test Liquid B; IEC 112 | ||
| 500 V | 500 V | Test liquid A; IEC 112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 13.0 - 16.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 7.22 - 8.89 μin/in-°F @Temperature 73.4 - 176 °F | DIN 53752 | ||
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | Melt; IEC 1006 | ||
| Thermal Conductivity | 0.270 W/m-K | 1.87 BTU-in/hr-ft2-°F | Melt; DIN 52612 | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | ISO 11357-3 | ||
| Maximum Service Temperature, Air | 120 °C | 248 °F | at 50% loss of tensile strength after 20000h; IEC 216-1 | ||
| 140 °C | 284 °F | at 50% loss of tensile strength after 5000h; IEC 216-1 | |||
| 200 °C | 392 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 245 - 270 °C | 473 - 518 °F | Injection molding | ||
| 230 - 290 °C | 446 - 554 °F | Coating | |||
| 260 °C | 500 °F | for shrinkage test | |||
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F | Ejection temperature | ||
| 60.0 °C | 140 °F | for shrinkage test | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | North America and Europe | ||||
| FDA | 21 CFR 177.1660 | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding and Coating | ||||
| Processing | Coating | ||||
| Film Extrusion | |||||
| Injection Molding | |||||
| Other Extrusion | |||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| Light stabilized or stable to light | |||||
| U.V. stabilized or stable to weather | |||||
| UL.UL-C | Yes | ||||