- 熔體流動速率 [g/10min]: 25.0
- 密度 [g/cm3]: 1.42
- 熱變形溫度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in3 | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | similar to ISO 62 test | ||
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 250 °C | 25 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1 | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1 | ||
| Tensile Modulus | 6.00 GPa | 870 ksi | ISO 527-1 | ||
| Charpy Impact Unnotched | 4.50 J/cm2 @Temperature -30.0 °C | 21.4 ft-lb/in2 @Temperature -22.0 °F | ISO 179-1eU | ||
| 4.50 J/cm2 @Temperature 23.0 °C | 21.4 ft-lb/in2 @Temperature 73.4 °F | ISO 179-1eU | |||
| Charpy Impact, Notched | 0.900 J/cm2 @Temperature -30.0 °C | 4.28 ft-lb/in2 @Temperature -22.0 °F | ISO 179-1eA | ||
| 0.900 J/cm2 @Temperature 23.0 °C | 4.28 ft-lb/in2 @Temperature 73.4 °F | ISO 179-1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 40.0 μm/m-°C | 22.2 μin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 90.0 μm/m-°C | 50.0 μin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Resin Type | PBT-GF15 | ||||