- 熔體流動速率 [g/10min]: 130.0
- 密度 [g/cm3]: 1.76
- 吸水率 [%]: 0.4
- 彎曲強度 [MPa]: 150.0
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.76 g/cc | 0.0636 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.12 % | 0.12 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Test | 75 cm3/g | 75 cm3/g | Viscosity number | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO Data | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO Data | ||
| Melt Flow | 130 g/10 min @Load 2.16 kg, Temperature 275 °C | 130 g/10 min @Load 4.76 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 150 MPa | 21800 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 1.2 % | 1.2 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 18.4 GPa | 2670 ksi | 1mm/min; ISO 527 | ||
| Charpy Impact, Notched | 1.00 J/cm2 | 4.76 ft-lb/in2 | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 4.5 @Frequency 1.00e+6 Hz | 4.5 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.7 @Frequency 100 Hz | 4.7 @Frequency 100 Hz | IEC 60250 | |||
| Dissipation Factor | 0.0020 @Frequency 100 Hz | 0.0020 @Frequency 100 Hz | IEC 60250 | ||
| 0.015 @Frequency 1.00e+6 Hz | 0.015 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 225 V | 225 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 25.0 μm/m-°C | 13.9 μin/in-°F | ISO 11359 | ||
| Melting Point | 223 °C | 433 °F | 10 K/min | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | BK15029 | ||||
| Commercial Status | North America and Europe | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||