- 熔體流動速率 [g/10min]: 45.0
- 密度 [g/cm3]: 1.81
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.81 g/cc | 0.0654 lb/in3 | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | similar to ISO 62 test | ||
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | ISO 294-4 | ||
| Melt Flow | 45 g/10 min @Load 2.16 kg, Temperature 260 °C | 45 g/10 min @Load 4.76 lb, Temperature 500 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 45.0 MPa | 6530 psi | ISO 527-1 | ||
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1 | ||
| Tensile Modulus | 4.00 GPa | 580 ksi | ISO 527-1 | ||
| Charpy Impact Unnotched | 1.50 J/cm2 | 7.14 ft-lb/in2 | ISO 179-1eU | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | UL Registered; IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Resin Type | (PBT+X)-MD40 | ||||