- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.22
- 吸水率 [%]: 0.01
- 缺口沖擊強度: 0.267
- 拉伸強度 [MPa]: 62.1
- 斷裂伸長率 [%]: 86.0
- 彎曲強度 [MPa]: 6.99
- 彎曲模量 [MPa]: 3.20
- 硬度: 90.0
- 熱變形溫度 [℃]: 150.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 - 1.80 g/cc | 0.0441 - 0.0650 lb/in3 | Average value: 1.46 g/cc Grade Count:245 |
| Filler Content | 15.0 - 20.0 % | 15.0 - 20.0 % | Average value: 17.0 % Grade Count:54 |
| Water Absorption | 0.0100 - 0.780 % | 0.0100 - 0.780 % | Average value: 0.231 % Grade Count:85 |
| Moisture Absorption at Equilibrium | 0.0300 - 0.200 % | 0.0300 - 0.200 % | Average value: 0.142 % Grade Count:96 |
| Water Absorption at Saturation | 0.310 - 0.450 % | 0.310 - 0.450 % | Average value: 0.394 % Grade Count:7 |
| Viscosity | 35000 - 1.66e+6 cP @Temperature 230 - 270 °C | 35000 - 1.66e+6 cP @Temperature 446 - 518 °F | Average value: 270000 cP Grade Count:7 |
| 35000 - 1.66e+6 cP @Shear Rate 100 - 10000 1/s | 35000 - 1.66e+6 cP @Shear Rate 100 - 10000 1/s | Average value: 270000 cP Grade Count:7 | |
| Viscosity Test | 69.0 - 116 cm3/g | 69.0 - 116 cm3/g | Average value: 97.1 cm3/g Grade Count:20 |
| Maximum Moisture Content | 0.0200 | 0.0200 | Average value: 0.0200 Grade Count:8 |
| Linear Mold Shrinkage | 0.00100 - 0.0225 cm/cm | 0.00100 - 0.0225 in/in | Average value: 0.00632 cm/cm Grade Count:181 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00500 - 0.00800 cm/cm | 0.00500 - 0.00800 in/in | Average value: 0.00600 cm/cm Grade Count:3 |
| Linear Mold Shrinkage, Transverse | 0.00100 - 0.0200 cm/cm | 0.00100 - 0.0200 in/in | Average value: 0.0103 cm/cm Grade Count:71 |
| Melt Flow | 2.00 - 131 g/10 min | 2.00 - 131 g/10 min | Average value: 25.2 g/10 min Grade Count:91 |
| Ash | 15.0 - 24.0 % | 15.0 - 24.0 % | Average value: 17.4 % Grade Count:8 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 83.0 - 109 | 83.0 - 109 | Average value: 91.5 Grade Count:24 |
| Hardness, Rockwell R | 90.0 - 120 | 90.0 - 120 | Average value: 117 Grade Count:27 |
| Ball Indentation Hardness | 153 - 190 MPa | 22200 - 27600 psi | Average value: 179 MPa Grade Count:5 |
| Tensile Strength, Ultimate | 6.99 - 140 MPa | 1010 - 20300 psi | Average value: 89.0 MPa Grade Count:195 |
| 40.0 - 182 MPa @Temperature -40.0 - 150 °C | 5800 - 26400 psi @Temperature -40.0 - 302 °F | Average value: 51.1 MPa Grade Count:9 | |
| 2.204 - 175 MPa @Temperature -40.0 - 160 °C | 319.7 - 25400 psi @Temperature -40.0 - 320 °F | Average value: 51.1 MPa Grade Count:9 | |
| 2.204 - 175 MPa @Strain 0.100 - 20.8 % | 319.7 - 25400 psi @Strain 0.100 - 20.8 % | Average value: 51.1 MPa Grade Count:9 | |
| Tensile Strength, Yield | 62.1 - 125 MPa | 9000 - 18100 psi | Average value: 99.8 MPa Grade Count:58 |
| Elongation at Break | 1.00 - 120 % | 1.00 - 120 % | Average value: 4.48 % Grade Count:207 |
| 1.90 - 8.00 % @Temperature -40.0 - 150 °C | 1.90 - 8.00 % @Temperature -40.0 - 302 °F | Average value: 4.58 % Grade Count:6 | |
| Elongation at Yield | 2.54 - 3.50 % | 2.54 - 3.50 % | Average value: 3.11 % Grade Count:5 |
| Modulus of Elasticity | 2.60 - 10.2 GPa | 377 - 1470 ksi | Average value: 6.54 GPa Grade Count:141 |
| 2.06843 - 6.60 GPa @Temperature -40.0 - 176 °C | 300.005 - 957 ksi @Temperature -40.0 - 349 °F | Average value: 4.17 GPa Grade Count:5 | |
| Flexural Yield Strength | 86.0 - 190 MPa | 12500 - 27600 psi | Average value: 153 MPa Grade Count:169 |
| 45.0 - 242 MPa @Temperature -40.0 - 150 °C | 6530 - 35100 psi @Temperature -40.0 - 302 °F | Average value: 93.8 MPa Grade Count:4 | |
| Flexural Modulus | 3.20 - 10.0 GPa | 464 - 1450 ksi | Average value: 5.67 GPa Grade Count:174 |
| 1.70 - 7.241 GPa @Temperature -40.0 - 150 °C | 247 - 1050 ksi @Temperature -40.0 - 302 °F | Average value: 3.50 GPa Grade Count:5 | |
| Compressive Yield Strength | 107 - 161 MPa | 15500 - 23400 psi | Average value: 126 MPa Grade Count:3 |
| Shear Modulus | 1.17 - 1.87 GPa | 170 - 271 ksi | Average value: 1.58 GPa Grade Count:6 |
| 0.0710 - 2.22 GPa @Temperature -50.0 - 200 °C | 10.3 - 322 ksi @Temperature -58.0 - 392 °F | Average value: 0.949 GPa Grade Count:6 | |
| Izod Impact, Notched | 0.267 - 1.60 J/cm | 0.500 - 3.00 ft-lb/in | Average value: 0.621 J/cm Grade Count:106 |
| 0.430 - 0.640 J/cm @Temperature -40.0 - -20.0 °C | 0.806 - 1.20 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.573 J/cm Grade Count:5 | |
| Izod Impact, Unnotched | 0.588 - 8.17 J/cm | 1.10 - 15.3 ft-lb/in | Average value: 5.80 J/cm Grade Count:18 |
| 6.45 - 7.36 J/cm @Temperature -40.0 - -40.0 °C | 12.1 - 13.8 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 6.90 J/cm Grade Count:2 | |
| Izod Impact, Notched (ISO) | 3.50 - 60.0 kJ/m2 | 1.67 - 28.6 ft-lb/in2 | Average value: 8.60 kJ/m2 Grade Count:76 |
| 4.00 - 10.0 kJ/m2 @Temperature -40.0 - 30.0 °C | 1.90 - 4.76 ft-lb/in2 @Temperature -40.0 - 86.0 °F | Average value: 6.87 kJ/m2 Grade Count:23 | |
| Izod Impact, Unnotched (ISO) | 12.2 - 65.0 kJ/m2 | 5.81 - 30.9 ft-lb/in2 | Average value: 47.3 kJ/m2 Grade Count:37 |
| 10.5 - 60.0 kJ/m2 @Temperature -40.0 - 30.0 °C | 5.00 - 28.6 ft-lb/in2 @Temperature -40.0 - 86.0 °F | Average value: 39.9 kJ/m2 Grade Count:14 | |
| Charpy Impact Unnotched | 1.45 - 10.0 J/cm2 | 6.90 - 47.6 ft-lb/in2 | Average value: 4.45 J/cm2 Grade Count:91 |
| 1.39 - 6.50 J/cm2 @Temperature -40.0 - 30.0 °C | 6.62 - 30.9 ft-lb/in2 @Temperature -40.0 - 86.0 °F | Average value: 3.79 J/cm2 Grade Count:60 | |
| Charpy Impact, Notched | 0.350 - 2.00 J/cm2 | 1.67 - 9.52 ft-lb/in2 | Average value: 0.760 J/cm2 Grade Count:110 |
| 0.350 - 1.00 J/cm2 @Temperature -40.0 - 30.0 °C | 1.67 - 4.76 ft-lb/in2 @Temperature -40.0 - 86.0 °F | Average value: 0.704 J/cm2 Grade Count:61 | |
| Dart Drop, Total Energy | 5.00 J | 3.69 ft-lb | Average value: 5.00 J Grade Count:3 |
| Puncture Energy | 1.80 - 10.6 J | 1.33 - 7.82 ft-lb | Average value: 4.07 J Grade Count:4 |
| 1.80 - 1.80 J @Temperature -30.0 - -30.0 °C | 1.33 - 1.33 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 1.80 J Grade Count:1 | |
| Tensile Creep Modulus, 1 hour | 0.000 - 7300 MPa | 0.000 - 1.06e+6 psi | Average value: 930 MPa Grade Count:12 |
| 0.000 - 60.0 MPa @Temperature 60.0 - 60.0 °C | 0.000 - 8700 psi @Temperature 140 - 140 °F | Average value: 30.0 MPa Grade Count:1 | |
| 0.000 - 60.0 MPa @Strain 0.000 - 1.96 % | 0.000 - 8700 psi @Strain 0.000 - 1.96 % | Average value: 30.0 MPa Grade Count:1 | |
| Tensile Creep Modulus, 1000 hours | 0.000 - 6900 MPa | 0.000 - 1.00e+6 psi | Average value: 811 MPa Grade Count:13 |
| 0.000 - 60.0 MPa @Temperature 60.0 - 60.0 °C | 0.000 - 8700 psi @Temperature 140 - 140 °F | Average value: 30.0 MPa Grade Count:1 | |
| 0.000 - 60.0 MPa @Strain 0.000 - 2.16 % | 0.000 - 8700 psi @Strain 0.000 - 2.16 % | Average value: 30.0 MPa Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+11 - 1.00e+17 ohm-cm | 1.00e+11 - 1.00e+17 ohm-cm | Average value: 1.46e+16 ohm-cm Grade Count:139 |
| Surface Resistance | 1.00e+13 - 3.00e+17 ohm | 1.00e+13 - 3.00e+17 ohm | Average value: 1.17e+16 ohm Grade Count:84 |
| Dielectric Constant | 2.70 - 4.60 | 2.70 - 4.60 | Average value: 3.60 Grade Count:97 |
| Dielectric Strength | 15.0 - 100 kV/mm | 381 - 2540 kV/in | Average value: 24.8 kV/mm Grade Count:123 |
| Dissipation Factor | 0.00100 - 0.0290 | 0.00100 - 0.0290 | Average value: 0.0105 Grade Count:67 |
| Dielectric Loss Index | 0.00200 - 0.0200 | 0.00200 - 0.0200 | Average value: 0.0187 Grade Count:14 |
| Arc Resistance | 0.000 - 180 sec | 0.000 - 180 sec | Average value: 107 sec Grade Count:27 |
| Comparative Tracking Index | 125 - 600 V | 125 - 600 V | Average value: 316 V Grade Count:91 |
| Hot Wire Ignition, HWI | 7.00 - 60.0 sec | 7.00 - 60.0 sec | Average value: 26.7 sec Grade Count:6 |
| High Amp Arc Ignition, HAI | 30.0 - 120 arcs | 30.0 - 120 arcs | Average value: 111 arcs Grade Count:6 |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 150 mm/min | 1.00 - 5.91 in/min | Average value: 99.5 mm/min Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.300 - 500 μm/m-°C | 0.167 - 278 μin/in-°F | Average value: 114 μm/m-°C Grade Count:86 |
| CTE, linear, Transverse to Flow | 9.50 - 141 μm/m-°C | 5.28 - 78.3 μin/in-°F | Average value: 99.7 μm/m-°C Grade Count:44 |
| Specific Heat Capacity | 1.50 - 1.84 J/g-°C | 0.359 - 0.440 BTU/lb-°F | Average value: 1.65 J/g-°C Grade Count:5 |
| Thermal Conductivity | 0.150 - 0.280 W/m-K | 1.04 - 1.94 BTU-in/hr-ft2-°F | Average value: 0.205 W/m-K Grade Count:7 |
| Melting Point | 200 - 255 °C | 392 - 491 °F | Average value: 224 °C Grade Count:108 |
| Maximum Service Temperature, Air | 75.0 - 330 °C | 167 - 626 °F | Average value: 173 °C Grade Count:21 |
| Transformation Temperature, Tg | 44.0 - 60.0 °C | 111 - 140 °F | Average value: 56.3 °C Grade Count:7 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 - 225 °C | 302 - 437 °F | Average value: 214 °C Grade Count:176 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 - 217 °C | 149 - 423 °F | Average value: 193 °C Grade Count:216 |
| Deflection Temperature at 5.0 MPa | 150 - 178 °C | 302 - 352 °F | Average value: 165 °C Grade Count:4 |
| Deflection Temperature at 8.0 MPa | 65.0 - 140 °C | 149 - 284 °F | Average value: 102 °C Grade Count:21 |
| Vicat Softening Point | 145 - 220 °C | 293 - 428 °F | Average value: 206 °C Grade Count:53 |
| Glass Transition Temp, Tg | 49.0 - 110 °C | 120 - 230 °F | Average value: 72.7 °C Grade Count:7 |
| UL RTI, Electrical | 50.0 - 140 °C | 122 - 284 °F | Average value: 130 °C Grade Count:22 |
| UL RTI, Mechanical with Impact | 50.0 - 140 °C | 122 - 284 °F | Average value: 124 °C Grade Count:22 |
| UL RTI, Mechanical without Impact | 50.0 - 140 °C | 122 - 284 °F | Average value: 128 °C Grade Count:22 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:221 |
| Oxygen Index | 19.0 - 35.0 % | 19.0 - 35.0 % | Average value: 23.0 % Grade Count:30 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 827 °C Grade Count:44 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 270 °C | 68.0 - 518 °F | Average value: 131 °C Grade Count:42 |
| Feed Temperature | 50.0 - 250 °C | 122 - 482 °F | Average value: 162 °C Grade Count:33 |
| Nozzle Temperature | 225 - 270 °C | 437 - 518 °F | Average value: 249 °C Grade Count:39 |
| Die Temperature | 240 - 275 °C | 464 - 527 °F | Average value: 257 °C Grade Count:20 |
| Melt Temperature | 203 - 280 °C | 397 - 536 °F | Average value: 247 °C Grade Count:118 |
| Mold Temperature | 30.0 - 130 °C | 86.0 - 266 °F | Average value: 79.5 °C Grade Count:128 |
| Injection Velocity | 70.0 - 300 mm/sec | 2.76 - 11.8 in/sec | Average value: 255 mm/sec Grade Count:14 |
| Drying Temperature | 80.0 - 140 °C | 176 - 284 °F | Average value: 121 °C Grade Count:95 |
| Dry Time | 2.00 - 12.0 hour | 2.00 - 12.0 hour | Average value: 3.82 hour Grade Count:94 |
| Moisture Content | 0.000 - 0.400 % | 0.000 - 0.400 % | Average value: 0.0526 % Grade Count:71 |
| Dew Point | -30.0 - -28.9 °C | -22.0 - -20.0 °F | Average value: -29.2 °C Grade Count:14 |
| Injection Pressure | 6.89 - 120 MPa | 1000 - 17400 psi | Average value: 80.8 MPa Grade Count:46 |
| Hold Pressure | 30.0 - 100 MPa | 4350 - 14500 psi | Average value: 61.1 MPa Grade Count:29 |
| Back Pressure | 0.000 - 18.0 MPa | 0.000 - 2610 psi | Average value: 4.65 MPa Grade Count:32 |
| Shot Size | 40.0 - 80.0 % | 40.0 - 80.0 % | Average value: 60.0 % Grade Count:3 |
| Screw Speed | 40.0 - 120 rpm | 40.0 - 120 rpm | Average value: 83.9 rpm Grade Count:27 |
| Hot-Working Temperature | 250 - 275 °C | 482 - 527 °F | Average value: 258 °C Grade Count:20 |