- 密度 [g/cm3]: 1.54
- 缺口沖擊強度: 0.534
- 彎曲模量 [MPa]: 5.17
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 95.1 MPa @Thickness 3.17 mm | 13800 psi @Thickness 0.125 in | ASTM D638 |
| Elongation at Break | 2.5 % @Thickness 3.17 mm | 2.5 % @Thickness 0.125 in | ASTM D638 |
| Flexural Strength | 148 MPa @Thickness 3.17 mm | 21500 psi @Thickness 0.125 in | ASTM D790 |
| Flexural Modulus | 5.17 GPa @Thickness 3.17 mm | 750 ksi @Thickness 0.125 in | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 182 °C | 360 °F | ASTM D648 |
| UL RTI, Electrical | 75.0 °C | 167 °F | |
| UL RTI, Mechanical with Impact | 75.0 °C | 167 °F | |
| UL RTI, Mechanical without Impact | 75.0 °C | 167 °F | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |