- 熔體流動速率 [g/10min]: 5.5
- 密度 [g/cm3]: 1.22
- 吸水率 [%]: 0.06
- 缺口沖擊強度: 0.64
- 斷裂伸長率 [%]: 47.0
- 彎曲強度 [MPa]: 26.0
- 彎曲模量 [MPa]: 1.67
- 硬度: 115.0
- 熱變形溫度 [℃]: 86.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 - 1.76 g/cc | 0.0439 - 0.0636 lb/in3 | Average value: 1.50 g/cc Grade Count:39 |
| Filler Content | 10.0 - 40.0 % | 10.0 - 40.0 % | Average value: 23.8 % Grade Count:8 |
| Water Absorption | 0.0600 - 0.100 % | 0.0600 - 0.100 % | Average value: 0.0733 % Grade Count:9 |
| Moisture Absorption at Equilibrium | 0.100 - 0.200 % | 0.100 - 0.200 % | Average value: 0.155 % Grade Count:6 |
| Linear Mold Shrinkage | 0.000 - 0.0220 cm/cm | 0.000 - 0.0220 in/in | Average value: 0.00469 cm/cm Grade Count:23 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00300 - 0.0120 cm/cm | 0.00300 - 0.0120 in/in | Average value: 0.00567 cm/cm Grade Count:6 |
| Linear Mold Shrinkage, Transverse | 0.00500 - 0.0220 cm/cm | 0.00500 - 0.0220 in/in | Average value: 0.00917 cm/cm Grade Count:8 |
| Melt Flow | 5.50 - 23.0 g/10 min | 5.50 - 23.0 g/10 min | Average value: 12.2 g/10 min Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 115 - 119 | 115 - 119 | Average value: 117 Grade Count:10 |
| Tensile Strength, Ultimate | 26.0 - 153 MPa | 3770 - 22200 psi | Average value: 101 MPa Grade Count:38 |
| Elongation at Break | 1.10 - 247 % | 1.10 - 247 % | Average value: 15.9 % Grade Count:39 |
| Modulus of Elasticity | 1.76 - 10.7 GPa | 256 - 1550 ksi | Average value: 6.79 GPa Grade Count:17 |
| Flexural Yield Strength | 47.0 - 210 MPa | 6820 - 30500 psi | Average value: 154 MPa Grade Count:39 |
| Flexural Modulus | 1.67 - 82.7 GPa | 243 - 12000 ksi | Average value: 9.31 GPa Grade Count:38 |
| Izod Impact, Notched | 0.640 - 52.9 J/cm | 1.20 - 99.0 ft-lb/in | Average value: 3.97 J/cm Grade Count:19 |
| 1.6017 - 1.6017 J/cm @Temperature -28.9 - -28.9 °C | 3.0006 - 3.0006 ft-lb/in @Temperature -20.0 - -20.0 °F | Average value: 1.60 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 5.34 - 10.7 J/cm | 10.0 - 20.0 ft-lb/in | Average value: 7.48 J/cm Grade Count:12 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 - NB | 2.38 ft-lb/in2 - NB | Average value: 8.23 kJ/m2 Grade Count:9 |
| <= 10.0 kJ/m2 @Temperature -40.0 - -30.0 °C | <= 4.76 ft-lb/in2 @Temperature -40.0 - -22.0 °F | Average value: 10.0 kJ/m2 Grade Count:1 | |
| Izod Impact, Unnotched (ISO) | 17.0 - 55.0 kJ/m2 | 8.09 - 26.2 ft-lb/in2 | Average value: 37.3 kJ/m2 Grade Count:3 |
| Charpy Impact Unnotched | 2.20 - 1000 J/cm2 | 10.5 - 4760 ft-lb/in2 | Average value: 4.54 J/cm2 Grade Count:6 |
| 2.20 - 999.9 J/cm2 @Temperature -30.0 - 30.0 °C | 10.5 - 4759 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 3.47 J/cm2 Grade Count:5 | |
| Charpy Impact, Notched | 0.390 - 8.00 J/cm2 | 1.86 - 38.1 ft-lb/in2 | Average value: 1.01 J/cm2 Grade Count:22 |
| 0.400 - 1.90 J/cm2 @Temperature -30.0 - 30.0 °C | 1.90 - 9.04 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 0.948 J/cm2 Grade Count:6 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+7 - 1.20e+17 ohm-cm | 1.00e+7 - 1.20e+17 ohm-cm | Average value: 1.71e+16 ohm-cm Grade Count:25 |
| Surface Resistance | 2.00e+10 - 4.00e+17 ohm | 2.00e+10 - 4.00e+17 ohm | Average value: 7.64e+16 ohm Grade Count:14 |
| Dielectric Constant | 2.80 - 4.30 | 2.80 - 4.30 | Average value: 3.64 Grade Count:8 |
| Dielectric Strength | 16.5 - 32.0 kV/mm | 420 - 813 kV/in | Average value: 23.5 kV/mm Grade Count:16 |
| Dissipation Factor | 0.000 - 0.0240 | 0.000 - 0.0240 | Average value: 0.0141 Grade Count:8 |
| Arc Resistance | 87.0 - 129 sec | 87.0 - 129 sec | Average value: 107 sec Grade Count:4 |
| Comparative Tracking Index | 175 - 600 V | 175 - 600 V | Average value: 302 V Grade Count:11 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 16.2 - 130 μm/m-°C | 9.00 - 72.2 μin/in-°F | Average value: 35.8 μm/m-°C Grade Count:16 |
| CTE, linear, Transverse to Flow | 35.0 - 116 μm/m-°C | 19.4 - 64.4 μin/in-°F | Average value: 77.6 μm/m-°C Grade Count:13 |
| Melting Point | 107 - 225 °C | 225 - 437 °F | Average value: 207 °C Grade Count:11 |
| Transformation Temperature, Tg | 20.0 - 71.0 °C | 68.0 - 160 °F | Average value: 50.3 °C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 - 228 °C | 187 - 442 °F | Average value: 198 °C Grade Count:20 |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 - 211 °C | 120 - 412 °F | Average value: 179 °C Grade Count:37 |
| Vicat Softening Point | 128 - 220 °C | 262 - 428 °F | Average value: 183 °C Grade Count:3 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:32 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 257 °C | 68.0 - 495 °F | Average value: 133 °C Grade Count:19 |
| Feed Temperature | 230 - 260 °C | 446 - 500 °F | Average value: 237 °C Grade Count:9 |
| Nozzle Temperature | 240 - 270 °C | 464 - 518 °F | Average value: 257 °C Grade Count:4 |
| Die Temperature | 240 - 260 °C | 464 - 500 °F | Average value: 254 °C Grade Count:8 |
| Melt Temperature | 230 - 270 °C | 446 - 518 °F | Average value: 246 °C Grade Count:11 |
| Mold Temperature | 30.0 - 107 °C | 86.0 - 225 °F | Average value: 83.6 °C Grade Count:15 |
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | Average value: 126 °C Grade Count:5 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.80 hour Grade Count:5 |
| 4.00 - 8.00 hour @Temperature 120 - 120 °C | 4.00 - 8.00 hour @Temperature 248 - 248 °F | Average value: 6.00 hour Grade Count:1 | |
| Moisture Content | 0.000 - 0.0200 % | 0.000 - 0.0200 % | Average value: 0.0180 % Grade Count:5 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 84.4 MPa Grade Count:9 |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | Average value: 0.172 MPa Grade Count:3 |
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | Average value: 255 °C Grade Count:8 |