- 熔體流動速率 [g/10min]: 5.0
- 密度 [g/cm3]: 1.13
- 缺口沖擊強度: 0.25
- 拉伸強度 [MPa]: 30.0
- 斷裂伸長率 [%]: 55.0
- 彎曲強度 [MPa]: 34.0
- 彎曲模量 [MPa]: 1.57
- 硬度: 116.0
- 熱變形溫度 [℃]: 95.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 - 1.75 g/cc | 0.0408 - 0.0632 lb/in3 | Average value: 1.48 g/cc Grade Count:139 |
| Filler Content | 15.0 - 35.0 % | 15.0 - 35.0 % | Average value: 25.5 % Grade Count:10 |
| Water Absorption | 0.000 - 0.900 % | 0.000 - 0.900 % | Average value: 0.127 % Grade Count:51 |
| Moisture Absorption at Equilibrium | 0.0300 - 0.500 % | 0.0300 - 0.500 % | Average value: 0.104 % Grade Count:55 |
| Water Absorption at Saturation | 0.350 - 0.500 % | 0.350 - 0.500 % | Average value: 0.438 % Grade Count:4 |
| Linear Mold Shrinkage | 0.00170 - 0.0260 cm/cm | 0.00170 - 0.0260 in/in | Average value: 0.0103 cm/cm Grade Count:128 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00400 - 0.0230 cm/cm | 0.00400 - 0.0230 in/in | Average value: 0.0180 cm/cm Grade Count:4 |
| Linear Mold Shrinkage, Transverse | 0.00170 - 0.0300 cm/cm | 0.00170 - 0.0300 in/in | Average value: 0.0104 cm/cm Grade Count:22 |
| Melt Flow | 5.00 - 82.0 g/10 min | 5.00 - 82.0 g/10 min | Average value: 29.8 g/10 min Grade Count:30 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 79.0 - 88.0 | 79.0 - 88.0 | Average value: 84.6 Grade Count:5 |
| Hardness, Rockwell R | 116 - 124 | 116 - 124 | Average value: 119 Grade Count:31 |
| Tensile Strength, Ultimate | 34.0 - 147 MPa | 4930 - 21300 psi | Average value: 73.1 MPa Grade Count:67 |
| Tensile Strength, Yield | 30.0 - 148 MPa | 4350 - 21500 psi | Average value: 81.4 MPa Grade Count:84 |
| Elongation at Break | 2.00 - 145 % | 2.00 - 145 % | Average value: 18.0 % Grade Count:79 |
| Elongation at Yield | 2.00 - 75.0 % | 2.00 - 75.0 % | Average value: 15.1 % Grade Count:22 |
| Modulus of Elasticity | 0.750 - 11.0 GPa | 109 - 1600 ksi | Average value: 3.96 GPa Grade Count:38 |
| Flexural Yield Strength | 55.0 - 216 MPa | 7980 - 31300 psi | Average value: 130 MPa Grade Count:115 |
| 35.0 - 35.0 MPa @Temperature 90.0 - 90.0 °C | 5080 - 5080 psi @Temperature 194 - 194 °F | Average value: 35.0 MPa Grade Count:1 | |
| Flexural Modulus | 1.57 - 11.0 GPa | 228 - 1600 ksi | Average value: 5.54 GPa Grade Count:123 |
| 0.600 - 0.600 GPa @Temperature 90.0 - 90.0 °C | 87.0 - 87.0 ksi @Temperature 194 - 194 °F | Average value: 0.600 GPa Grade Count:1 | |
| Izod Impact, Notched | 0.250 - 5.34 J/cm | 0.468 - 10.0 ft-lb/in | Average value: 0.757 J/cm Grade Count:65 |
| 1.53 - 1.53 J/cm @Temperature -30.0 - -30.0 °C | 2.87 - 2.87 ft-lb/in @Temperature -22.0 - -22.0 °F | Average value: 1.53 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 0.588 J/cm - NB | 1.10 ft-lb/in - NB | Average value: 8.22 J/cm Grade Count:9 |
| Izod Impact, Notched (ISO) | 4.00 - 45.0 kJ/m2 | 1.90 - 21.4 ft-lb/in2 | Average value: 8.60 kJ/m2 Grade Count:50 |
| 2.00 - 10.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 0.952 - 4.76 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 6.00 kJ/m2 Grade Count:3 | |
| Izod Impact, Unnotched (ISO) | 30.0 - 80.0 kJ/m2 | 14.3 - 38.1 ft-lb/in2 | Average value: 52.5 kJ/m2 Grade Count:44 |
| Charpy Impact Unnotched | 2.50 J/cm2 - NB | 11.9 ft-lb/in2 - NB | Average value: 6.76 J/cm2 Grade Count:25 |
| 2.50 - 999.9 J/cm2 @Temperature -30.0 - -20.0 °C | 11.9 - 4759 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 8.63 J/cm2 Grade Count:19 | |
| Charpy Impact, Notched | 0.160 - 4.50 J/cm2 | 0.761 - 21.4 ft-lb/in2 | Average value: 0.791 J/cm2 Grade Count:27 |
| 0.200 - 1.00 J/cm2 @Temperature -30.0 - -20.0 °C | 0.952 - 4.76 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 0.647 J/cm2 Grade Count:17 | |
| Gardner Impact | 9.49 - 43.0 J | 7.00 - 31.7 ft-lb | Average value: 32.9 J Grade Count:3 |
| Tensile Impact Strength | 45.0 - 100 kJ/m2 | 21.4 - 47.6 ft-lb/in2 | Average value: 65.0 kJ/m2 Grade Count:3 |
| Tensile Creep Modulus, 1 hour | 950 - 3000 MPa | 138000 - 435000 psi | Average value: 2280 MPa Grade Count:7 |
| Tensile Creep Modulus, 1000 hours | 650 - 1800 MPa | 94300 - 261000 psi | Average value: 1410 MPa Grade Count:7 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+8 - 1.00e+17 ohm-cm | 1.00e+8 - 1.00e+17 ohm-cm | Average value: 1.55e+16 ohm-cm Grade Count:102 |
| Surface Resistance | 1.00e+8 - 1.00e+17 ohm | 1.00e+8 - 1.00e+17 ohm | Average value: 3.68e+15 ohm Grade Count:33 |
| Dielectric Constant | 2.80 - 4.00 | 2.80 - 4.00 | Average value: 3.24 Grade Count:82 |
| Dielectric Strength | 15.0 - 42.9 kV/mm | 381 - 1090 kV/in | Average value: 22.0 kV/mm Grade Count:101 |
| Dissipation Factor | 0.00100 - 0.0300 | 0.00100 - 0.0300 | Average value: 0.0135 Grade Count:26 |
| Dielectric Loss Index | 0.00100 - 0.0200 | 0.00100 - 0.0200 | Average value: 0.0183 Grade Count:44 |
| Arc Resistance | 21.0 - 120 sec | 21.0 - 120 sec | Average value: 97.1 sec Grade Count:16 |
| Comparative Tracking Index | 50.0 - 600 V | 50.0 - 600 V | Average value: 332 V Grade Count:27 |
| Hot Wire Ignition, HWI | 15.0 - 120 sec | 15.0 - 120 sec | Average value: 49.5 sec Grade Count:3 |
| High Amp Arc Ignition, HAI | 15.0 - 120 arcs | 15.0 - 120 arcs | Average value: 58.5 arcs Grade Count:3 |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | Average value: 138 mm/min Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 16.2 - 139 μm/m-°C | 9.00 - 77.2 μin/in-°F | Average value: 70.0 μm/m-°C Grade Count:46 |
| 124 - 124 μm/m-°C @Temperature 60.0 - 138 °C | 68.9 - 68.9 μin/in-°F @Temperature 140 - 280 °F | Average value: 124 μm/m-°C Grade Count:1 | |
| CTE, linear, Transverse to Flow | 84.0 - 120 μm/m-°C | 46.7 - 66.7 μin/in-°F | Average value: 102 μm/m-°C Grade Count:13 |
| Thermal Conductivity | 0.173 - 0.202 W/m-K | 1.20 - 1.40 BTU-in/hr-ft2-°F | Average value: 0.192 W/m-K Grade Count:3 |
| Melting Point | 200 - 240 °C | 392 - 464 °F | Average value: 222 °C Grade Count:26 |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 - 225 °C | 203 - 437 °F | Average value: 185 °C Grade Count:96 |
| Deflection Temperature at 1.8 MPa (264 psi) | 40.0 - 220 °C | 104 - 428 °F | Average value: 134 °C Grade Count:122 |
| Deflection Temperature at 8.0 MPa | 46.0 - 48.0 °C | 115 - 118 °F | Average value: 47.5 °C Grade Count:6 |
| Vicat Softening Point | 110 - 216 °C | 230 - 421 °F | Average value: 177 °C Grade Count:22 |
| UL RTI, Electrical | 60.0 - 140 °C | 140 - 284 °F | Average value: 90.0 °C Grade Count:5 |
| UL RTI, Mechanical with Impact | 60.0 - 130 °C | 140 - 266 °F | Average value: 88.6 °C Grade Count:5 |
| UL RTI, Mechanical without Impact | 60.0 - 140 °C | 140 - 284 °F | Average value: 94.3 °C Grade Count:5 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:135 |
| Oxygen Index | 28.0 - 32.0 % | 28.0 - 32.0 % | Average value: 30.2 % Grade Count:6 |
| Glow Wire Test | 850 - 960 °C | 1560 - 1760 °F | Average value: 942 °C Grade Count:11 |
| Shrinkage | 0.400 - 0.400 % @Temperature 150 - 150 °C | 0.400 - 0.400 % @Temperature 302 - 302 °F | Average value: 0.400 % Grade Count:1 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 204 - 270 °C | 400 - 518 °F | Average value: 247 °C Grade Count:7 |
| Nozzle Temperature | 225 - 280 °C | 437 - 536 °F | Average value: 243 °C Grade Count:36 |
| Melt Temperature | 190 - 280 °C | 374 - 536 °F | Average value: 243 °C Grade Count:57 |
| Mold Temperature | 37.8 - 121 °C | 100 - 250 °F | Average value: 72.7 °C Grade Count:60 |
| Drying Temperature | 100 - 140 °C | 212 - 284 °F | Average value: 121 °C Grade Count:24 |
| Dry Time | 3.00 - 6.00 hour | 3.00 - 6.00 hour | Average value: 4.00 hour Grade Count:23 |
| 2.00 - 4.00 hour @Temperature 121 - 121 °C | 2.00 - 4.00 hour @Temperature 250 - 250 °F | Average value: 3.00 hour Grade Count:1 | |
| Moisture Content | 0.0100 - 0.300 % | 0.0100 - 0.300 % | Average value: 0.0693 % Grade Count:10 |
| Injection Pressure | 4.96 - 140 MPa | 720 - 20300 psi | Average value: 76.3 MPa Grade Count:42 |
| Back Pressure | 0.000 - 20.0 MPa | 0.000 - 2900 psi | Average value: 8.76 MPa Grade Count:33 |
| Shot Size | 30.0 - 80.0 % | 30.0 - 80.0 % | Average value: 53.3 % Grade Count:6 |
| Vent Depth | 0.00127 - 0.00381 cm | 0.000500 - 0.00150 in | Average value: 0.00222 cm Grade Count:4 |
| Screw Speed | 20.0 - 100 rpm | 20.0 - 100 rpm | Average value: 91.3 rpm Grade Count:32 |