- 密度 [g/cm3]: 1.33
- 缺口沖擊強度: 0.214
- 拉伸強度 [MPa]: 49.0
- 斷裂伸長率 [%]: 68.0
- 彎曲強度 [MPa]: 40.0
- 彎曲模量 [MPa]: 2.06
- 熱變形溫度 [℃]: 213.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 - 1.67 g/cc | 0.0480 - 0.0603 lb/in3 | Average value: 1.45 g/cc Grade Count:16 |
| Linear Mold Shrinkage | 0.000500 - 0.00910 cm/cm | 0.000500 - 0.00910 in/in | Average value: 0.00366 cm/cm Grade Count:9 |
| Linear Mold Shrinkage, Transverse | 0.00800 - 0.0110 cm/cm | 0.00800 - 0.0110 in/in | Average value: 0.00958 cm/cm Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 40.0 - 175 MPa | 5800 - 25400 psi | Average value: 105 MPa Grade Count:16 |
| Tensile Strength, Yield | 49.0 - 142 MPa | 7110 - 20600 psi | Average value: 104 MPa Grade Count:6 |
| Elongation at Break | 1.00 - 7.00 % | 1.00 - 7.00 % | Average value: 3.03 % Grade Count:16 |
| Modulus of Elasticity | 2.28 - 22.4 GPa | 331 - 3250 ksi | Average value: 10.4 GPa Grade Count:10 |
| Flexural Yield Strength | 68.0 - 269 MPa | 9860 - 39000 psi | Average value: 157 MPa Grade Count:16 |
| Flexural Modulus | 2.06 - 22.9 GPa | 299 - 3320 ksi | Average value: 11.9 GPa Grade Count:16 |
| Izod Impact, Notched | 0.214 - 0.740 J/cm | 0.401 - 1.39 ft-lb/in | Average value: 0.462 J/cm Grade Count:12 |
| Izod Impact, Unnotched | 0.907 - 6.41 J/cm | 1.70 - 12.0 ft-lb/in | Average value: 4.10 J/cm Grade Count:12 |
| Falling Dart Impact | 4.34 - 7.57 J | 3.20 - 5.58 ft-lb | Average value: 5.62 J Grade Count:7 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.500 - 100000 ohm-cm | 0.500 - 100000 ohm-cm | Average value: 6170 ohm-cm Grade Count:11 |
| Surface Resistance | 100 - 1.00e+10 ohm | 100 - 1.00e+10 ohm | Average value: 3.51e+8 ohm Grade Count:13 |
| Static Decay | 0.0100 - 2.00 sec | 0.0100 - 2.00 sec | Average value: 1.00 sec Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 1.10 - 1.20 W/m-K | 7.63 - 8.33 BTU-in/hr-ft2-°F | Average value: 1.13 W/m-K Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 213 - 221 °C | 415 - 430 °F | Average value: 218 °C Grade Count:5 |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 - 216 °C | 178 - 421 °F | Average value: 191 °C Grade Count:13 |
| Flammability, UL94 | HB | HB | Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 243 - 282 °C | 469 - 540 °F | Average value: 256 °C Grade Count:6 |
| Melt Temperature | 238 - 282 °C | 460 - 540 °F | Average value: 256 °C Grade Count:15 |
| Mold Temperature | 37.8 - 107 °C | 100 - 225 °F | Average value: 81.7 °C Grade Count:15 |
| Drying Temperature | 121 - 135 °C | 250 - 275 °F | Average value: 122 °C Grade Count:15 |
| Dry Time | 3.00 - 12.0 hour | 3.00 - 12.0 hour | Average value: 5.82 hour Grade Count:14 |
| Moisture Content | 0.0200 - 0.150 % | 0.0200 - 0.150 % | Average value: 0.0500 % Grade Count:15 |
| Dew Point | -28.9 °C | -20.0 °F | Average value: -28.9 °C Grade Count:6 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:6 |
| Back Pressure | 0.172 - 0.689 MPa | 24.9 - 99.9 psi | Average value: 0.431 MPa Grade Count:9 |
| Clamp Pressure | 41.0 - 83.0 MPa | 5950 - 12000 psi | Average value: 58.5 MPa Grade Count:6 |
| Shot Size | 40.0 - 80.0 % | 40.0 - 80.0 % | Average value: 60.0 % Grade Count:6 |
| Vent Depth | 0.00250 - 0.00380 cm | 0.000984 - 0.00150 in | Average value: 0.00315 cm Grade Count:6 |
| Screw Speed | 50.0 - 100 rpm | 50.0 - 100 rpm | Average value: 70.0 rpm Grade Count:6 |