- 缺口沖擊強(qiáng)度: 0.8
- 斷裂伸長(zhǎng)率 [%]: 186.2
- 彎曲強(qiáng)度 [MPa]: 110.3
- 彎曲模量 [MPa]: 7.58
- 硬度: 118.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 110.3 MPa | 16000 psi | ASTM D638 |
| Flexural Yield Strength | 186.2 MPa | 27010 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm @Thickness 3.17 mm | 1.50 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm | HB @Thickness 0.0625 in | |