- 熔體流動速率 [g/10min]: 15.0
- 密度 [g/cm3]: 1.21
- 吸水率 [%]: 0.03
- 缺口沖擊強度: 5.34
- 拉伸強度 [MPa]: 53.0
- 彎曲模量 [MPa]: 2.00
- 熱變形溫度 [℃]: 101.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in3 | ASTM D792 |
| Water Absorption | 0.030 % @Time 86400 sec | 0.030 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage | 0.0075 - 0.010 cm/cm | 0.0075 - 0.010 in/in | ASTM D955 |
| Melt Flow | 15 g/10 min @Load 3.80 kg, Temperature 250 °C | 15 g/10 min @Load 8.38 lb, Temperature 482 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 53.0 MPa @Thickness 3.17 mm | 7690 psi @Thickness 0.125 in | ASTM D638 |
| Elongation at Break | 115 % @Thickness 3.17 mm | 115 % @Thickness 0.125 in | ASTM D638 |
| Flexural Strength | 82.0 MPa @Thickness 3.17 mm | 11900 psi @Thickness 0.125 in | ASTM D790 |
| Flexural Modulus | 2.00 GPa @Thickness 3.17 mm | 290 ksi @Thickness 0.125 in | ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm @Temperature -20.0 °C | 10.0 ft-lb/in @Temperature -4.00 °F | ASTM D256 |
| 8.01 J/cm @Thickness 3.17 mm | 15.0 ft-lb/in @Thickness 0.125 in | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | ASTM D648 |
| UL RTI, Electrical | 75.0 °C | 167 °F | |
| UL RTI, Mechanical with Impact | 75.0 °C | 167 °F | |
| UL RTI, Mechanical without Impact | 75.0 °C | 167 °F | |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||