- 密度 [g/cm3]: 1.52
- 吸水率 [%]: 0.02
- 缺口沖擊強度: 0.587
- 斷裂伸長率 [%]: 109
- 彎曲強度 [MPa]: 76.0
- 彎曲模量 [MPa]: 6.60
- 熱變形溫度 [℃]: 203.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 - 1.89 g/cc | 0.0549 - 0.0683 lb/in3 | Average value: 1.70 g/cc Grade Count:29 |
| Filler Content | 30.0 - 50.0 % | 30.0 - 50.0 % | Average value: 38.0 % Grade Count:5 |
| Water Absorption | 0.0200 - 0.100 % | 0.0200 - 0.100 % | Average value: 0.0425 % Grade Count:8 |
| Moisture Absorption at Equilibrium | 0.0200 - 0.0400 % | 0.0200 - 0.0400 % | Average value: 0.0233 % Grade Count:6 |
| Linear Mold Shrinkage | 0.000 - 0.00300 cm/cm | 0.000 - 0.00300 in/in | Average value: 0.00116 cm/cm Grade Count:17 |
| Linear Mold Shrinkage, Transverse | 0.00200 - 0.0110 cm/cm | 0.00200 - 0.0110 in/in | Average value: 0.00543 cm/cm Grade Count:20 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 43.0 - 79.0 | 43.0 - 79.0 | Average value: 62.1 Grade Count:8 |
| Tensile Strength, Ultimate | 76.0 - 175 MPa | 11000 - 25400 psi | Average value: 130 MPa Grade Count:29 |
| 48.0 - 200 MPa @Temperature -40.0 - 150 °C | 6960 - 29000 psi @Temperature -40.0 - 302 °F | Average value: 86.6 MPa Grade Count:1 | |
| 17.0 - 216 MPa @Temperature -40.0 - 250 °C | 2470 - 31300 psi @Temperature -40.0 - 482 °F | Average value: 86.6 MPa Grade Count:1 | |
| 17.0 - 216 MPa @Thickness 1.60 - 3.17 mm | 2470 - 31300 psi @Thickness 0.0630 - 0.125 in | Average value: 86.6 MPa Grade Count:1 | |
| Elongation at Break | 1.20 - 5.50 % | 1.20 - 5.50 % | Average value: 3.45 % Grade Count:27 |
| 2.50 - 3.20 % @Temperature 120 - 150 °C | 2.50 - 3.20 % @Temperature 248 - 302 °F | Average value: 2.06 % Grade Count:1 | |
| 0.700 - 3.20 % @Temperature -40.0 - 250 °C | 0.700 - 3.20 % @Temperature -40.0 - 482 °F | Average value: 2.06 % Grade Count:1 | |
| 0.700 - 3.20 % @Thickness 1.60 - 3.17 mm | 0.700 - 3.20 % @Thickness 0.0630 - 0.125 in | Average value: 2.06 % Grade Count:1 | |
| Modulus of Elasticity | 7.50 - 22.0 GPa | 1090 - 3190 ksi | Average value: 12.0 GPa Grade Count:26 |
| 4.80 - 11.6 GPa @Temperature -40.0 - 150 °C | 696 - 1680 ksi @Temperature -40.0 - 302 °F | Average value: 7.45 GPa Grade Count:1 | |
| 2.77 - 16.5 GPa @Temperature -40.0 - 250 °C | 402 - 2390 ksi @Temperature -40.0 - 482 °F | Average value: 7.45 GPa Grade Count:1 | |
| 2.77 - 16.5 GPa @Thickness 1.60 - 3.17 mm | 402 - 2390 ksi @Thickness 0.0630 - 0.125 in | Average value: 7.45 GPa Grade Count:1 | |
| Flexural Yield Strength | 109 - 220 MPa | 15800 - 31900 psi | Average value: 151 MPa Grade Count:26 |
| 42.0 - 260 MPa @Temperature -40.0 - 150 °C | 6090 - 37700 psi @Temperature -40.0 - 302 °F | Average value: 109 MPa Grade Count:2 | |
| 42.0 - 260 MPa @Thickness 0.800 - 3.17 mm | 6090 - 37700 psi @Thickness 0.0315 - 0.125 in | Average value: 109 MPa Grade Count:2 | |
| Flexural Modulus | 6.60 - 20.0 GPa | 957 - 2900 ksi | Average value: 11.3 GPa Grade Count:29 |
| 3.30 - 16.7 GPa @Temperature -40.0 - 150 °C | 479 - 2420 ksi @Temperature -40.0 - 302 °F | Average value: 7.38 GPa Grade Count:2 | |
| 3.30 - 16.7 GPa @Thickness 0.800 - 3.17 mm | 479 - 2420 ksi @Thickness 0.0315 - 0.125 in | Average value: 7.38 GPa Grade Count:2 | |
| Compressive Yield Strength | 51.7 - 131 MPa | 7500 - 19000 psi | Average value: 79.3 MPa Grade Count:9 |
| Compressive Modulus | 9.50 - 21.5 GPa | 1380 - 3120 ksi | Average value: 13.5 GPa Grade Count:8 |
| Izod Impact, Notched | 0.587 - 1.60 J/cm | 1.10 - 3.00 ft-lb/in | Average value: 1.12 J/cm Grade Count:4 |
| Izod Impact, Notched (ISO) | 3.50 - 60.0 kJ/m2 | 1.67 - 28.6 ft-lb/in2 | Average value: 22.9 kJ/m2 Grade Count:17 |
| Izod Impact, Unnotched (ISO) | 22.0 - 126 kJ/m2 | 10.5 - 60.0 ft-lb/in2 | Average value: 46.3 kJ/m2 Grade Count:6 |
| Charpy Impact Unnotched | 5.00 - 10.0 J/cm2 | 23.8 - 47.6 ft-lb/in2 | Average value: 7.30 J/cm2 Grade Count:6 |
| 4.00 - 4.00 J/cm2 @Temperature -30.0 - -30.0 °C | 19.0 - 19.0 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 4.00 J/cm2 Grade Count:2 | |
| Charpy Impact, Notched | 0.360 - 5.90 J/cm2 | 1.71 - 28.1 ft-lb/in2 | Average value: 1.56 J/cm2 Grade Count:19 |
| 0.700 - 0.800 J/cm2 @Temperature -30.0 - -30.0 °C | 3.33 - 3.81 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 0.750 J/cm2 Grade Count:2 | |
| Tensile Impact Strength | 40.0 - 80.0 kJ/m2 | 19.0 - 38.1 ft-lb/in2 | Average value: 56.7 kJ/m2 Grade Count:3 |
| Coefficient of Friction | 0.120 - 0.210 | 0.120 - 0.210 | Average value: 0.172 Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 - 2.00e+16 ohm-cm | 1.00e+12 - 2.00e+16 ohm-cm | Average value: 3.85e+15 ohm-cm Grade Count:17 |
| Surface Resistance | 1.00e+15 - 1.00e+17 ohm | 1.00e+15 - 1.00e+17 ohm | Average value: 1.57e+16 ohm Grade Count:17 |
| Dielectric Constant | 2.90 - 6.70 | 2.90 - 6.70 | Average value: 3.78 Grade Count:18 |
| 4.00 - 4.20 @Temperature 120 - 250 °C | 4.00 - 4.20 @Temperature 248 - 482 °F | Average value: 4.06 Grade Count:2 | |
| 4.00 - 4.20 @Frequency 1.00e+9 - 1.00e+10 Hz | 4.00 - 4.20 @Frequency 1.00e+9 - 1.00e+10 Hz | Average value: 4.06 Grade Count:2 | |
| Dielectric Strength | 26.0 - 49.0 kV/mm | 660 - 1240 kV/in | Average value: 38.0 kV/mm Grade Count:10 |
| Dissipation Factor | 0.00100 - 0.0340 | 0.00100 - 0.0340 | Average value: 0.0137 Grade Count:18 |
| 0.00500 - 0.0290 @Temperature 120 - 250 °C | 0.00500 - 0.0290 @Temperature 248 - 482 °F | Average value: 0.0149 Grade Count:2 | |
| 0.00500 - 0.0290 @Frequency 1.00e+9 - 1.00e+10 Hz | 0.00500 - 0.0290 @Frequency 1.00e+9 - 1.00e+10 Hz | Average value: 0.0149 Grade Count:2 | |
| Arc Resistance | 145 - 183 sec | 145 - 183 sec | Average value: 172 sec Grade Count:8 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | Average value: 202 V Grade Count:17 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | -10.0 - 15.0 μm/m-°C | -5.56 - 8.33 μin/in-°F | Average value: 5.69 μm/m-°C Grade Count:18 |
| -4.00 - 20.0 μm/m-°C @Temperature 55.0 - 260 °C | -2.22 - 11.1 μin/in-°F @Temperature 131 - 500 °F | Average value: 8.00 μm/m-°C Grade Count:3 | |
| -4.00 - 20.0 μm/m-°C @Thickness 2.00 - 4.00 mm | -2.22 - 11.1 μin/in-°F @Thickness 0.0787 - 0.157 in | Average value: 8.00 μm/m-°C Grade Count:3 | |
| CTE, linear, Transverse to Flow | 11.0 - 69.0 μm/m-°C | 6.11 - 38.3 μin/in-°F | Average value: 42.1 μm/m-°C Grade Count:18 |
| 34.0 - 62.0 μm/m-°C @Temperature 55.0 - 260 °C | 18.9 - 34.4 μin/in-°F @Temperature 131 - 500 °F | Average value: 47.7 μm/m-°C Grade Count:3 | |
| 34.0 - 62.0 μm/m-°C @Thickness 2.00 - 4.00 mm | 18.9 - 34.4 μin/in-°F @Thickness 0.0787 - 0.157 in | Average value: 47.7 μm/m-°C Grade Count:3 | |
| Melting Point | 280 - 350 °C | 536 - 662 °F | Average value: 317 °C Grade Count:25 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Average value: 130 °C Grade Count:6 |
| Deflection Temperature at 0.46 MPa (66 psi) | 203 - 275 °C | 397 - 527 °F | Average value: 246 °C Grade Count:4 |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 - 295 °C | 365 - 563 °F | Average value: 234 °C Grade Count:29 |
| Vicat Softening Point | 149 - 238 °C | 300 - 460 °F | Average value: 194 °C Grade Count:5 |
| UL RTI, Electrical | 130 - 240 °C | 266 - 464 °F | Average value: 161 °C Grade Count:12 |
| UL RTI, Mechanical with Impact | 130 - 220 °C | 266 - 428 °F | Average value: 156 °C Grade Count:12 |
| UL RTI, Mechanical without Impact | 130 - 240 °C | 266 - 464 °F | Average value: 185 °C Grade Count:6 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:20 |
| Oxygen Index | 40.0 - 47.0 % | 40.0 - 47.0 % | Average value: 43.5 % Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 150 °C | 68.0 - 302 °F | Average value: 66.3 °C Grade Count:10 |
| Feed Temperature | 40.0 - 120 °C | 104 - 248 °F | Average value: 71.1 °C Grade Count:9 |
| Die Temperature | 290 - 375 °C | 554 - 707 °F | Average value: 337 °C Grade Count:9 |
| Melt Temperature | 270 - 399 °C | 518 - 750 °F | Average value: 335 °C Grade Count:21 |
| Mold Temperature | 30.0 - 160 °C | 86.0 - 320 °F | Average value: 86.6 °C Grade Count:15 |
| Injection Velocity | 150 mm/sec | 5.91 in/sec | Average value: 150 mm/sec Grade Count:3 |
| Drying Temperature | 149 - 170 °C | 300 - 338 °F | Average value: 153 °C Grade Count:19 |
| Dry Time | 3.00 - 8.00 hour | 3.00 - 8.00 hour | Average value: 4.53 hour Grade Count:19 |
| Moisture Content | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:17 |
| Dew Point | -40.0 - -28.9 °C | -40.0 - -20.0 °F | Average value: -38.0 °C Grade Count:10 |
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | Average value: 100 MPa Grade Count:11 |
| Hold Pressure | 48.0 - 150 MPa | 6960 - 21800 psi | Average value: 88.8 MPa Grade Count:9 |
| Back Pressure | 3.00 MPa | 435 psi | Average value: 3.00 MPa Grade Count:7 |
| Screw Speed | 80.0 - 200 rpm | 80.0 - 200 rpm | Average value: 139 rpm Grade Count:7 |
| Hot-Working Temperature | 285 - 375 °C | 545 - 707 °F | Average value: 336 °C Grade Count:8 |