- 熔體流動速率 [g/10min]: 1.9
- 密度 [g/cm3]: 0.905
- 彎曲模量 [MPa]: 0.750
- 熱變形溫度 [℃]: 60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ISO 1183 |
| Melt Flow | 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C | 1.9 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Modulus | 0.400 GPa | 58.0 ksi | MD/TD; ISO 527-3 |
| Flexural Modulus | 0.750 GPa | 109 ksi | 50% humidity; ISO 178 |
| Dart Drop, Total Energy | 40.0 J @Thickness 0.0500 mm | 29.5 ft-lb @Thickness 0.00197 in | 1300N; ISO 7765-2 |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 140 °C | 284 °F | ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ISO 75-2 |
| Vicat Softening Point | 128 °C | 262 °F | A50; ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 1.0 % | <= 1.0 % | ASTM D1003 |
| Gloss | >= 150 % | >= 150 % | 20° of arc; ASTM D2457 |