- 熔體流動速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.98
- 拉伸強度 [MPa]: 37.0
- 熱變形溫度 [℃]: 64.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.980 g/cc | 0.0354 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | mold average, Borealis Method | ||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C | 20 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527-2 | ||
| Tensile Modulus | 2.60 GPa | 377 ksi | 1mm/min; ISO 527-2 | ||
| Charpy Impact Unnotched | 2.50 J/cm2 @Temperature -20.0 °C | 11.9 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU | ||
| 7.00 J/cm2 @Temperature 23.0 °C | 33.3 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.150 J/cm2 @Temperature -20.0 °C | 0.714 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | ||
| 0.350 J/cm2 @Temperature 23.0 °C | 1.67 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Hot Ball Pressure Test | 125 °C @Thickness 2.00 mm | 257 °F @Thickness 0.0787 in | EN 60695-10-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C | 147 °F | ISO 75-2 | ||
| 120 °C | 248 °F | ISO 75-2 | |||
| Vicat Softening Point | 94.0 °C @Load 5.10 kg | 201 °F @Load 11.2 lb | ISO 527-2 | ||
| 155 °C @Load 1.02 kg | 311 °F @Load 2.25 lb | ISO 527-2 | |||
| Flammability, UL94 | HB @Thickness 2.00 mm | HB @Thickness 0.0787 in | |||
| Flammability Test | 23 @Thickness 3.00 mm | 23 @Thickness 0.118 in | FMVSS 302; mm/min; DIN 75200 | ||
| Glow Wire Test | 800 °C @Thickness 2.00 mm | 1470 °F @Thickness 0.0787 in | ignition temperature; EN 60695-2-13 | ||
| 825 °C @Thickness 2.00 mm | 1520 °F @Thickness 0.0787 in | flammability index; EN 60695-2-12 | |||
| Optical Properties | Metric | English | Comments | ||
| Gloss | 50 % | 50 % | 2mm plaque, 20° of arc; DIN 67530 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 220 - 260 °C | 428 - 500 °F | mass temperature | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |||
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi | |||
| Descriptive Properties | |||||
| Back Pressure | low to medium | ||||
| Emission (μgC/g) | 35 | VDA 277 | |||
| Fogging (mg) | 1.4 | 100°C, 16h, DIN 75201 | |||
| Screw Speed | low to medium | ||||