- 熔體流動速率 [g/10min]: 9.0
- 密度 [g/cm3]: 0.97
- 缺口沖擊強度: 5.6
- 拉伸強度 [MPa]: 18.0
- 彎曲模量 [MPa]: 1.30
- 熱變形溫度 [℃]: 92.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.970 g/cc | 0.0350 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | post shrinkage (2h/90°C) | ||
| 0.010 cm/cm | 0.010 in/in | mold average | |||
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 9.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 33.0 MPa | 4790 psi | 132 N/10 s; ISO 2039 | ||
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Break | >= 80 % | >= 80 % | ISO 527-2 | ||
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527-2 | ||
| Tensile Modulus | 1.25 GPa | 181 ksi | 1mm/min; ISO 527-2 | ||
| Flexural Strength | 23.0 MPa | 3340 psi | ISO 178 | ||
| Flexural Modulus | 1.30 GPa | 189 ksi | 2mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.60 kJ/m2 @Temperature -20.0 °C | 2.66 ft-lb/in2 @Temperature -4.00 °F | ISO 180/1A | ||
| 55.0 kJ/m2 @Temperature 23.0 °C | 26.2 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | |||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | ||
| NB @Temperature -20.0 °C | NB @Temperature -4.00 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.450 J/cm2 @Temperature -30.0 °C | 2.14 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.800 J/cm2 @Temperature -20.0 °C | 3.81 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |||
| 5.00 J/cm2 @Temperature 23.0 °C | 23.8 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 80.0 μm/m-°C | 44.4 μin/in-°F | (-30°C/80°C); Borealis Method | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C | 120 °F | ISO 75-2 | ||
| Vicat Softening Point | 43.0 °C @Load 5.10 kg | 109 °F @Load 11.2 lb | ISO 306 | ||
| 128 °C @Load 1.02 kg | 262 °F @Load 2.25 lb | ISO 306 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 220 - 260 °C | 428 - 500 °F | mass temperature | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |||
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi | |||
| Descriptive Properties | |||||
| Back Pressure | low to medium | ||||
| Screw Speed | low to medium | ||||