- 熔體流動速率 [g/10min]: 2.8
- 密度 [g/cm3]: 2.0
- 拉伸強度 [MPa]: 18.0
- 熱變形溫度 [℃]: 110.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.00 g/cc | 0.0723 lb/in3 | ISO 1183 |
| Filler Content | 70 % | 70 % | |
| Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.8 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | 50mm/min; ISO 527-2 |
| Elongation at Break | 50 % | 50 % | 50mm/min; ISO 527-2 |
| Elongation at Yield | 1.8 % | 1.8 % | ISO 527-2 |
| Tensile Modulus | 3.50 GPa | 508 ksi | 1mm/min; ISO 527-2 |
| Charpy Impact, Notched | 0.120 J/cm2 @Temperature -20.0 °C | 0.571 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA |
| 0.190 J/cm2 @Temperature 23.0 °C | 0.904 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ISO 75-2 |
| Vicat Softening Point | 105 °C | 221 °F | B50; ISO 306 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 200 - 220 °C | 392 - 428 °F | cylinder |
| Die Temperature | 210 - 220 °C | 410 - 428 °F | |
| Melt Temperature | 210 - 230 °C | 410 - 446 °F | |