- 熔體流動速率 [g/10min]: 2.8
- 密度 [g/cm3]: 0.905
- 拉伸強度 [MPa]: 39.5
- 彎曲模量 [MPa]: 2.00
- 熱變形溫度 [℃]: 118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ISO 1183 |
| Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.8 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 39.5 MPa | 5730 psi | 50mm/min; ISO 527-2 |
| Film Elongation at Break, MD | 158 % | 158 % | blown films; ISO 527-3 |
| 450 % | 450 % | cast films; ISO 527-3 | |
| Film Elongation at Break, TD | 4.0 % | 4.0 % | blown films; ISO 527-3 |
| 5.0 % | 5.0 % | cast films; ISO 527-3 | |
| Elongation at Yield | 7.0 % | 7.0 % | ISO 527-2 |
| Tensile Modulus | 1.55 GPa | 225 ksi | roll stack films TD; ISO 527-3 |
| 1.70 GPa | 247 ksi | roll stack films MD; ISO 527-3 | |
| 1.70 GPa | 247 ksi | cast films TD; ISO 527-3 | |
| 1.875 GPa | 271.9 ksi | cast films MD; ISO 527-3 | |
| 2.05 GPa | 297 ksi | blown films MD; ISO 527-3 | |
| 2.07 GPa | 300 ksi | blown films TD; ISO 527-3 | |
| Flexural Modulus | 2.00 GPa | 290 ksi | 50% humidity; ISO 178 |
| Charpy Impact, Notched | 0.400 J/cm2 @Temperature 23.0 °C | 1.90 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA |
| Dart Drop, Total Energy | 1.00 J @Thickness 0.0500 mm | 0.738 ft-lb @Thickness 0.00197 in | cast films; ISO 7765-2 |
| 1.00 J @Thickness 0.300 mm | 0.738 ft-lb @Thickness 0.0118 in | roll stack films; ISO 7765-2 | |
| Coefficient of Friction | 0.30 - 0.40 | 0.30 - 0.40 | film to film; cast; ISO 8295 |
| 0.30 - 0.40 | 0.30 - 0.40 | film to film;blown; ISO 8295 | |
| Dart drop Test | >= 25.0 g @Thickness 0.0500 mm | >= 0.0551 lb @Thickness 0.00197 in | blown films; ISO 7765-1 |
| Film Tensile Strength at Break, MD | 42.0 MPa | 6090 psi | blown films; ISO 527-3 |
| 60.0 MPa | 8700 psi | cast films; ISO 527-3 | |
| Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | cast films; ISO 527-3 |
| 42.0 MPa | 6090 psi | blown films; ISO 527-3 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 166 °C | 331 °F | DSC; ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ISO 75-2 |
| Vicat Softening Point | 156 °C @Load 1.02 kg | 313 °F @Load 2.25 lb | A50; ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 5.0 % | <= 5.0 % | cast films; ASTM D1003 |
| <= 13.5 % | <= 13.5 % | roll stack films; ASTM D1003 | |
| <= 14 % | <= 14 % | blown films; ASTM D1003 | |
| Gloss | >= 45 % | >= 45 % | 20° of arc, blown films; ASTM D2457 |
| >= 110 % | >= 110 % | 20° of arc, cast films; ASTM D2457 | |
| >= 130 % | >= 130 % | 20° of arc, roll stack films; ASTM D2457 | |