- 熔體流動(dòng)速率 [g/10min]: 11.0
- 密度 [g/cm3]: 0.905
- 缺口沖擊強(qiáng)度: 12.0
- 拉伸強(qiáng)度 [MPa]: 19.0
- 彎曲模量 [MPa]: 0.900
- 熱變形溫度 [℃]: 75.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | post shrinkage (2h/90°C) | ||
| 0.014 cm/cm | 0.014 in/in | mold average | |||
| Melt Flow | 11 g/10 min @Load 2.16 kg, Temperature 230 °C | 11 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 55 | 55 | ISO 868 | ||
| Ball Indentation Hardness | 36.0 MPa | 5220 psi | 132N/10s; ISO 2039 | ||
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Break | >= 150 % | >= 150 % | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 5.5 % | 5.5 % | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 0.950 GPa | 138 ksi | 1mm/min; ISO 527-2 | ||
| Flexural Strength | 21.0 MPa | 3050 psi | ISO 178 | ||
| Flexural Modulus | 0.900 GPa | 131 ksi | 2mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 12.0 kJ/m2 @Temperature -20.0 °C | 5.71 ft-lb/in2 @Temperature -4.00 °F | ISO 180/1A | ||
| 57.0 kJ/m2 @Temperature 23.0 °C | 27.1 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | |||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | ||
| NB @Temperature -20.0 °C | NB @Temperature -4.00 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.700 J/cm2 @Temperature -30.0 °C | 3.33 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.850 J/cm2 @Temperature -20.0 °C | 4.04 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |||
| 7.00 J/cm2 @Temperature 23.0 °C | 33.3 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 100 μm/m-°C | 55.6 μin/in-°F | (-30°C/80°C); Borealis Method | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.0 °C | 118 °F | ISO 75-2 | ||
| Vicat Softening Point | 45.0 °C @Load 5.10 kg | 113 °F @Load 11.2 lb | ISO 306 | ||
| 135 °C @Load 1.02 kg | 275 °F @Load 2.25 lb | ISO 306 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 220 - 260 °C | 428 - 500 °F | mass temperature | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |||
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi | |||
| Descriptive Properties | |||||
| Back Pressure | low to medium | ||||
| Screw Speed | low to medium | ||||