- 熔體流動速率 [g/10min]: 2.8
- 密度 [g/cm3]: 0.905
- 拉伸強度 [MPa]: 35.0
- 彎曲模量 [MPa]: 1.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ISO 1183 |
| Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.8 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | 50mm/min; ISO 527-2 |
| Elongation at Yield | 9.0 % | 9.0 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 1.60 GPa | 232 ksi | 1mm/min; ISO 527-2 |
| Flexural Modulus | 1.50 GPa | 218 ksi | 5mm/min; ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 162 - 166 °C | 324 - 331 °F | ISO 3146 |
| Optical Properties | Metric | English | Comments |
| Haze | 27 % | 27 % | ASTM D1003 |