- 熔體流動速率 [g/10min]: 11.5
- 密度 [g/cm3]: 0.905
- 缺口沖擊強度: 8.5
- 拉伸強度 [MPa]: 21.0
- 彎曲模量 [MPa]: 1.00
- 熱變形溫度 [℃]: 82.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | Borealis Method | ||
| Melt Flow | 11.5 g/10 min @Load 2.16 kg, Temperature 230 °C | 11.5 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 43.0 MPa | 6240 psi | H 358/30; ISO 2039 | ||
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO 527-2 | ||
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Break | 150 % | 150 % | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 5.1 % | 5.1 % | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 1.10 GPa | 160 ksi | 1mm/min; ISO 527-2 | ||
| Flexural Strength | 22.5 MPa | 3260 psi | 3.5% strain; ISO 178 | ||
| 25.0 MPa | 3630 psi | ISO 178 | |||
| Flexural Modulus | 1.00 GPa | 145 ksi | 2mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 8.50 kJ/m2 @Temperature -20.0 °C | 4.04 ft-lb/in2 @Temperature -4.00 °F | ISO 180/1A | ||
| 50.0 kJ/m2 @Temperature 23.0 °C | 23.8 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 200 kJ/m2 @Temperature -20.0 °C | 95.2 ft-lb/in2 @Temperature -4.00 °F | ISO 180/1U | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 180/1U | |||
| Charpy Impact Unnotched | 22.0 J/cm2 @Temperature -20.0 °C | 105 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.900 J/cm2 @Temperature -20.0 °C | 4.28 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | ||
| 5.50 J/cm2 @Temperature 23.0 °C | 26.2 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 82.0 °C | 180 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | ISO 75-2 | ||
| Vicat Softening Point | 56.0 °C @Load 5.10 kg | 133 °F @Load 11.2 lb | ISO 306 | ||
| 143 °C @Load 1.02 kg | 289 °F @Load 2.25 lb | ISO 306 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 220 - 260 °C | 428 - 500 °F | mass temperature | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |||
| Hold Pressure | 3.00 - 6.00 MPa | 435 - 870 psi | |||
| Descriptive Properties | |||||
| Back Pressure | low to medium | ||||
| Emission (μgC/g) | < 50 | VDA 227 | |||
| Fogging (mg) | <2 | DIN 75201 | |||
| Screw Speed | low to medium | ||||