- 熔體流動速率 [g/10min]: 25.0
- 密度 [g/cm3]: 0.9
- 拉伸強度 [MPa]: 18.0
- 熱變形溫度 [℃]: 69.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | |||
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 230 °C | 25 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 15 % | 15 % | ISO 527-2 | ||
| Tensile Modulus | 0.850 GPa | 123 ksi | 1mm/min; ISO 527-2 | ||
| Charpy Impact, Notched | 0.300 J/cm2 @Temperature -20.0 °C | 1.43 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | ||
| 1.10 J/cm2 @Temperature 23.0 °C | 5.23 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 200 - 250 °C | 392 - 482 °F | |||
| Mold Temperature | 15.0 - 40.0 °C | 59.0 - 104 °F | |||
| Hold Pressure | 20.0 - 50.0 MPa | 2900 - 7250 psi | minimize | ||
| Descriptive Properties | |||||
| Injection Velocity | high | ||||