- 熔體流動速率 [g/10min]: 3.0
- 拉伸強度 [MPa]: 30.0
- 熱變形溫度 [℃]: 80.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | 50mm/min; ISO 527-2 |
| Tensile Modulus | 1.00 GPa | 145 ksi | 1mm/min; ISO 527-2 |
| Charpy Impact, Notched | 0.400 J/cm2 @Temperature 0.000 °C | 1.90 ft-lb/in2 @Temperature 32.0 °F | ISO 179/1eA |
| 1.50 J/cm2 @Temperature 23.0 °C | 7.14 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ISO 75-2 |
| Optical Properties | Metric | English | Comments |
| Haze | 9.0 % | 9.0 % | bottle, 6mm thick; Borealis Method |
| 15 % | 15 % | 2mm plaque; Borealis Method | |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 230 °C | 446 °F | |
| Die Temperature | 220 °C | 428 °F | |
| Melt Temperature | 230 °C | 446 °F | |