- 熔體流動速率 [g/10min]: 30.0
- 密度 [g/cm3]: 0.906
- 拉伸強度 [MPa]: 27.0
- 熱變形溫度 [℃]: 75.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.906 g/cc | 0.0327 lb/in3 | ISO 1183 |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 230 °C | 30 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | 50mm/min; ISO 527-2 |
| Elongation at Yield | 13 % | 13 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 1.05 GPa | 152 ksi | 1mm/min; ISO 527-3 |
| Charpy Impact, Notched | 0.600 J/cm2 @Temperature 23.0 °C | 2.86 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | ISO 75-2 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |