- 熔體流動速率 [g/10min]: 11.0
- 密度 [g/cm3]: 0.9
- 彎曲模量 [MPa]: 0.800
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.900 - 0.910 g/cc | 0.0325 - 0.0329 lb/in3 | ISO 1183 | ||
| Melt Flow | 11 g/10 min @Load 2.16 kg, Temperature 230 °C | 11 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 550 - 750 % | 550 - 750 % | ISO 527-3 | ||
| Tensile Modulus | 0.400 - 0.500 GPa | 58.0 - 72.5 ksi | MD/TD; ISO 527-3 | ||
| Flexural Modulus | 0.800 GPa | 116 ksi | ISO 178 | ||
| Dart Drop, Total Energy | 20.0 J @Thickness 0.0500 mm | 14.8 ft-lb @Thickness 0.00197 in | 1150N; ISO 7765-2 | ||
| Coefficient of Friction | <= 0.50 | <= 0.50 | film to film; ISO 8295 | ||
| Film Tensile Strength at Break, MD | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527-3 | ||
| Film Tensile Strength at Break, TD | 25.0 - 45.0 MPa | 3630 - 6530 psi | ISO 527-3 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 142 - 148 °C | 288 - 298 °F | DSC; ISO 3146 | ||
| Vicat Softening Point | 130 °C @Load 1.02 kg | 266 °F @Load 2.25 lb | A50; ISO 306 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | <= 2.0 % | <= 2.0 % | ASTM D1003 | ||
| Gloss | >= 120 % | >= 120 % | 20° of arc; ASTM D2457 | ||
| Component Elements Properties | Metric | English | Comments | ||
| SiO2 | 0.18 % | 0.18 % | Antiblock; Borealis Method | ||
| Descriptive Properties | |||||
| Metal Adhesion (tape test) | Excellent | Borealis Method | |||