- 熔體流動速率 [g/10min]: 90.0
- 密度 [g/cm3]: 0.904
- 拉伸強度 [MPa]: 25.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.904 g/cc | 0.0327 lb/in3 | ISO 1183 |
| Melt Flow | 90 g/10 min @Load 2.16 kg, Temperature 230 °C | 90 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50mm/min; ISO 527-2 |
| Elongation at Break | 10 % | 10 % | ISO 527-2 |
| Tensile Modulus | 1.30 GPa | 189 ksi | 1mm/min; ISO 527-2 |
| Charpy Impact Unnotched | 4.10 J/cm2 @Temperature -20.0 °C | 19.5 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU |
| 7.50 J/cm2 @Temperature 23.0 °C | 35.7 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 165 °C | 329 °F | ISO 3146 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 220 - 270 °C | 428 - 518 °F | mass temperature |
| Mold Temperature | 30.0 - 60.0 °C | 86.0 - 140 °F | |