- 熔體流動速率 [g/10min]: 30.0
- 密度 [g/cm3]: 0.91
- 拉伸強度 [MPa]: 27.0
- 硬度: 88.0
- 熱變形溫度 [℃]: 103.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | |||
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 230 °C | 30 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 88 | 88 | ISO 2309-2 | ||
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 5.0 % | 5.0 % | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 1.55 GPa | 225 ksi | 1mm/min; ISO 527-2 | ||
| Charpy Impact, Notched | 0.400 J/cm2 @Temperature -20.0 °C | 1.90 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | ||
| 0.700 J/cm2 @Temperature 23.0 °C | 3.33 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Puncture Energy | 20.0 J @Temperature -20.0 °C | 14.8 ft-lb @Temperature -4.00 °F | ISO 6603-2 | ||
| 24.0 J @Temperature 0.000 °C | 17.7 ft-lb @Temperature 32.0 °F | ISO 6603-2 | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | ISO 75-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | |||
| Mold Temperature | 10.0 - 30.0 °C | 50.0 - 86.0 °F | |||
| Hold Pressure | 20.0 - 50.0 MPa | 2900 - 7250 psi | |||
| Descriptive Properties | |||||
| Injection Velocity | highest possible | ||||