- 熔體流動速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.9
- 拉伸強度 [MPa]: 25.0
- 硬度: 89.0
- 熱變形溫度 [℃]: 95.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.013 - 0.014 cm/cm | 0.013 - 0.014 in/in | Borealis method | ||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C | 20 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 89 | 89 | ISO 2309-2 | ||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 6.0 % | 6.0 % | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 1.30 GPa | 189 ksi | 1mm/min; ISO 527-2 | ||
| Charpy Impact, Notched | 0.350 J/cm2 @Temperature -20.0 °C | 1.67 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | ||
| 0.750 J/cm2 @Temperature 23.0 °C | 3.57 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | ISO 75-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Middle Barrel Temperature | 220 - 260 °C | 428 - 500 °F | mass temperature | ||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |||
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi | |||
| Descriptive Properties | |||||
| Back Pressure | low to medium | ||||
| Screw Speed | low to medium | ||||