- 熔體流動速率 [g/10min]: 1.5
- 密度 [g/cm3]: 0.9
- 彎曲模量 [MPa]: 0.650
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 - 0.910 g/cc | 0.0325 - 0.0329 lb/in3 | ISO 1183 |
| Melt Flow | 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C | 1.5 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 550 - 600 % | 550 - 600 % | MD/TD; ISO 527-3 |
| Tensile Modulus | 0.730 GPa | 106 ksi | MD/TD; ISO 527-3 |
| Flexural Modulus | 0.650 GPa | 94.3 ksi | ISO 178 |
| Dart Drop, Total Energy | 50.0 J | 36.9 ft-lb | ISO 7765-1 |
| Coefficient of Friction | >= 0.70 | >= 0.70 | film to film; ISO 8295 |
| Film Tensile Strength at Break, MD | 30.0 - 40.0 MPa | 4350 - 5800 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 25.0 - 35.0 MPa | 3630 - 5080 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 133 - 136 °C | 271 - 277 °F | ISO 3146 |
| Vicat Softening Point | 115 °C @Load 1.02 kg | 239 °F @Load 2.25 lb | A50; ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 3.0 % | <= 3.0 % | ASTM D1003 |
| Gloss | >= 85 % | >= 85 % | 20° of arc; ASTM D2457 |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |