- 熔體流動速率 [g/10min]: 12.0
- 彎曲模量 [MPa]: 0.900
- 熱變形溫度 [℃]: 66.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 12 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Slip Level | 2000 ppm | 2000 ppm | EAA; Borealis Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Modulus | 0.500 GPa | 72.5 ksi | MD/TD; ISO 527-3 |
| Flexural Modulus | 0.900 GPa | 131 ksi | ISO 178 |
| Dart Drop, Total Energy | 20.0 J | 14.8 ft-lb | 1000N; ISO 7765-1 |
| Coefficient of Friction | 0.15 | 0.15 | film to film; ISO 8295 |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 143 °C | 289 °F | ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ISO 75-2 |
| Vicat Softening Point | 130 °C @Load 1.02 kg | 266 °F @Load 2.25 lb | A50; ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 1.5 % | <= 1.5 % | ASTM D1003 |
| Gloss | 140 % | 140 % | 20° of arc; ASTM D2457 |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |
| Component Elements Properties | Metric | English | Comments |
| SiO2 | 0.18 % | 0.18 % | Borealis Method |