- 熔體流動速率 [g/10min]: 2.8
- 密度 [g/cm3]: 0.926
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in3 | Exxon Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 2.8 g/10 min | 2.8 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 500 % | 500 % | ASTM D882 |
| Film Elongation at Break, TD | 850 % | 850 % | ASTM D882 |
| Secant Modulus, MD | 0.117 GPa | 17.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.117 GPa | 17.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 150 g | 150 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 200 g | 200 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 4.72 g/micron | 120 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 6.30 g/micron | 160 g/mil | ASTM D1922 |
| Dart Drop | 5.04 g/micron | 128 g/mil | F50; ASTM D1709 |
| Dart drop Test | 160 g | 0.353 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 102 °C | 216 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 5.0 % | 5.0 % | ASTM D1003 |
| Gloss | 74 % | 74 % | 45°, ASTM D-2457 |