- 熔體流動(dòng)速率 [g/10min]: 0.19
- 密度 [g/cm3]: 0.932
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.932 g/cc | 0.0337 lb/in3 | ExxonMobil Method |
| Vinyl Acetate Content | 10.1 % | 10.1 % | ExxonMobil Method |
| Melt Flow | 0.19 g/10 min | 0.19 g/10 min | 190°C, 2.16 kg; ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 |
| Film Elongation at Break, TD | 620 % | 620 % | ASTM D882 |
| Elmendorf Tear Strength, MD | 1.77 g/micron | 45.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 1.67 g/micron | 42.5 g/mil | ASTM D1922 |
| Dart Drop | 13.0 g/micron | 330 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 35.2 MPa | 5100 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 35.2 MPa | 5100 psi | ASTM D882 |
| 1% Secant Modulus, MD | 110 MPa | 16000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 124 MPa | 18000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 97.8 °C | 208 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 82.8 °C | 181 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 5.0 % | 5.0 % | ASTM D1003 |
| Gloss | 70 % | 70 % | 45°; ASTM D2457 |