- 熔體流動速率 [g/10min]: 1.5
- 密度 [g/cm3]: 0.941
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.941 g/cc | 0.0340 lb/in3 | ExxonMobil Method | ||
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | ASTM D1693 | ||
| Vinyl Acetate Content | 19.3 % | 19.3 % | ExxonMobil Method | ||
| Melt Flow | 1.5 g/10 min | 1.5 g/10 min | ExxonMobil Method | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 81 | 81 | 15s; ASTM D2240 | ||
| Hardness, Shore D | 30 | 30 | 15s; ASTM D2240 | ||
| Tensile Strength at Break | 13.1 MPa | 1900 psi | ASTM D638 | ||
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 | ||
| 1% Secant Modulus | 53.1 MPa | 7700 psi | ASTM D790 | ||
| Tensile Impact Strength | 630 kJ/m2 | 300 ft-lb/in2 | ASTM D1822 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 85.0 °C | 185 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Vicat Softening Point | 63.3 °C | 146 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.
Users of our Advanced Search (registration required) may exclude discontinued materials from search results.