- 密度 [g/cm3]: 0.953
- 彎曲模量 [MPa]: 0.0276
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.953 g/cc | 0.0344 lb/in3 | ExxonMobil Method |
| Viscosity | 2800 cP @Temperature 190 °C | 2800 cP @Temperature 374 °F | ASTM D3236 |
| Vinyl Acetate Content | 27.6 % | 27.6 % | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 68 | 68 | 15s; ASTM D2240 |
| Hardness, Shore D | 15 | 15 | 15s; ASTM D2240 |
| Tensile Strength at Break | 2.00 MPa | 290 psi | ASTM D638 |
| Elongation at Break | 240 % | 240 % | ASTM D638 |
| Flexural Modulus | 0.0276 GPa | 4.00 ksi | 1% secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 73.9 °C | 165 °F | Peak Melting Temperature; ExxonMobil Method |