- 熔體流動(dòng)速率 [g/10min]: 1.6
- 密度 [g/cm3]: 0.941
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.941 g/cc | 0.0340 lb/in3 | ExxonMobil Method |
| Vinyl Acetate Content | 18.5 % | 18.5 % | ExxonMobil Method |
| Melt Flow | 1.6 g/10 min | 1.6 g/10 min | 190°C, 2.16 kg; ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 180 % | 180 % | ASTM D882 |
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D882 |
| Elmendorf Tear Strength MD | 40 g | 40 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 80 g | 80 g | ASTM D1922 |
| Dart drop Test | 370 g | 0.816 lb | ASTM D1709A |
| Film Tensile Strength at Break, MD | 26.9 MPa | 3900 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 27.6 MPa | 4000 psi | ASTM D882 |
| 1% Secant Modulus, MD | 65.5 MPa | 9500 psi | ASTM D882 |
| 1% Secant Modulus, TD | 68.9 MPa | 10000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 86.1 °C | 187 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 62.2 °C | 144 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 28 % | 28 % | ASTM D1003 |
| Gloss | 49 % | 49 % | 45°; ASTM D2457 |