- 熔體流動速率 [g/10min]: 25.0
- 密度 [g/cm3]: 0.952
- 彎曲模量 [MPa]: 0.0186
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | ExxonMobil Method |
| Vinyl Acetate Content | 27.6 % | 27.6 % | ExxonMobil Method |
| Melt Flow | 25 g/10 min | 25 g/10 min | 190°C, 2.16 kg; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 70 | 70 | 15s; ASTM D2240 |
| Hardness, Shore D | 19 | 19 | 15s; ASTM D2240 |
| Tensile Strength at Break | 4.83 MPa | 700 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Flexural Modulus | 0.0186 GPa | 2.70 ksi | 1% secant; ASTM D790 |
| Impact Test | 14.9 J | 11.0 ft-lb | Instrument Impact, Total Energy at 23°C; ASTM D3763 |
| 25.8 J | 19.0 ft-lb | Instrument Impact, Total Energy at -40°C; ASTM D3763 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 66.1 °C | 151 °F | Peak Melting Temperature; ExxonMobil Method |