- 熔體流動(dòng)速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.935
- 拉伸強(qiáng)度 [MPa]: 5.24
- 彎曲模量 [MPa]: 0.0607
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in3 | ExxonMobil Method |
| Vinyl Acetate Content | 18.2 % | 18.2 % | ExxonMobil Method |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | 190°C, 2.16 kg; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 76 | 76 | 15s; ASTM D2240 |
| Hardness, Shore D | 36 | 36 | 15s; ASTM D2240 |
| Tensile Strength at Break | 11.7 MPa | 1700 psi | ASTM D638 |
| Tensile Strength, Yield | 5.24 MPa | 760 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Elongation at Yield | 260 % | 260 % | ASTM D638 |
| Flexural Modulus | 0.0607 GPa | 8.80 ksi | 1% secant; ASTM D790 |
| Impact Test | 17.6 J | 13.0 ft-lb | Instrument Impact, Total Energy at 23°C; ASTM D3763 |
| 35.3 J | 26.0 ft-lb | Instrument Impact, Total Energy at -40°C; ASTM D3763 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 87.2 °C | 189 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 63.9 °C | 147 °F | ASTM D1525 |