- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.926
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in3 | ExxonMobil Method | ||
| Vinyl Acetate Content | 5.8 % | 5.8 % | ExxonMobil Method | ||
| Thickness | 38.1 microns | 1.50 mil | |||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ExxonMobil Method | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 7.58 MPa | 1100 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 6.89 MPa | 1000 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 240 % | 240 % | ASTM D882 | ||
| Film Elongation at Break, TD | 670 % | 670 % | ASTM D882 | ||
| Impact Test | 0.813 J | 0.600 ft-lb | at -34°C; ASTM D4272 | ||
| 2.03 J | 1.50 ft-lb | at 23°C; ASTM D4272 | |||
| Elmendorf Tear Strength, MD | 8.27 g/micron | 210 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 2.36 g/micron | 60.0 g/mil | ASTM D1922 | ||
| Dart Drop | 4.33 g/micron | 110 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 34.5 MPa | 5000 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 22.4 MPa | 3250 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 138 MPa | 20000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 172 MPa | 25000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 103 °C | 217 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 3.0 % | 3.0 % | ASTM D1003 | ||
| Gloss | 76 % | 76 % | 45°; ASTM D2457 | ||
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||