- 熔體流動速率 [g/10min]: 1.3
- 密度 [g/cm3]: 0.923
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in3 | ExxonMobil Method | ||
| Vinyl Acetate Content | 3.5 % | 3.5 % | ExxonMobil Method | ||
| Thickness | 38.1 microns | 1.50 mil | |||
| Melt Flow | 1.3 g/10 min | 1.3 g/10 min | ExxonMobil Method | ||
| Antiblock Level | 3000 ppm | 3000 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 8.27 MPa | 1200 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 8.14 MPa | 1180 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 190 % | 190 % | ASTM D882 | ||
| Film Elongation at Break, TD | 580 % | 580 % | ASTM D882 | ||
| Film Elongation at Yield, MD | 6.7 % | 6.7 % | ASTM D882 | ||
| Film Elongation at Yield, TD | 5.7 % | 5.7 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 190 g | 190 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 110 g | 110 g | ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 4.984 g/micron | 126.6 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 2.887 g/micron | 73.33 g/mil | ASTM D1922 | ||
| Dart Drop | 4.461 g/micron | 113.3 g/mil | ASTM D1709 | ||
| Dart drop Test | 170 g | 0.375 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 24.2 MPa | 3510 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 23.2 MPa | 3370 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 146 MPa | 21200 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 172 MPa | 24900 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 105 °C | 221 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Crystallization Temperature | 92.0 °C | 198 °F | ExxonMobil Method | ||
| Vicat Softening Point | 88.3 °C | 191 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 6.5 % | 6.5 % | ASTM D1003 | ||
| Gloss | 69 % | 69 % | 45°; ASTM D2457 | ||
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||