- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.925
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in3 | ExxonMobil Method | ||
| Vinyl Acetate Content | 4.6 % | 4.6 % | ExxonMobil Method | ||
| Thickness | 38.1 microns | 1.50 mil | |||
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ExxonMobil Method | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 8.27 MPa | 1200 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 7.93 MPa | 1150 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 180 % | 180 % | ASTM D882 | ||
| Film Elongation at Break, TD | 580 % | 580 % | ASTM D882 | ||
| Film Elongation at Yield, MD | 6.9 % | 6.9 % | ASTM D882 | ||
| Film Elongation at Yield, TD | 5.6 % | 5.6 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 200 g | 200 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 90 g | 90 g | ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 5.248 g/micron | 133.3 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 2.36 g/micron | 60.0 g/mil | ASTM D1922 | ||
| Dart Drop | 4.984 g/micron | 126.6 g/mil | ASTM D1709 | ||
| Dart drop Test | 190 g | 0.419 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 25.9 MPa | 3760 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 24.7 MPa | 3580 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 146 MPa | 21200 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 168 MPa | 24400 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 104 °C | 220 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Crystallization Temperature | 91.0 °C | 196 °F | ExxonMobil Method | ||
| Vicat Softening Point | 88.9 °C | 192 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 6.4 % | 6.4 % | ASTM D1003 | ||
| Gloss | 71 % | 71 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||