- 熔體流動速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.944
- 彎曲模量 [MPa]: 0.0454
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.944 g/cc | 0.0341 lb/in3 | ExxonMobil Method | ||
| Vinyl Acetate Content | 22 % | 22 % | ExxonMobil Method | ||
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 78 | 78 | 15s; ASTM D2240 | ||
| Hardness, Shore D | 32 | 32 | 15s; ASTM D2240 | ||
| Tensile Strength at Break | 9.58 MPa | 1390 psi | ASTM D638 | ||
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 | ||
| Flexural Modulus | 0.0454 GPa | 6.58 ksi | 1% secant; ASTM D790 | ||
| Impact Test | 16.3 J | 12.0 ft-lb | Instrument Impact, Total Energy at 23°C; ASTM D3763 | ||
| 29.8 J | 22.0 ft-lb | Instrument Impact, Total Energy at -40°C; ASTM D3763 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 81.7 °C | 179 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Vicat Softening Point | 57.8 °C | 136 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.