- 熔體流動(dòng)速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.93
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in3 | ExxonMobil Method | ||
| Vinyl Acetate Content | 9.0 % | 9.0 % | ExxonMobil Method | ||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ExxonMobil Method | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 6.89 MPa | 1000 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 6.27 MPa | 910 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 330 % | 330 % | ASTM D882 | ||
| Film Elongation at Break, TD | 660 % | 660 % | ASTM D882 | ||
| Film Elongation at Yield, MD | 7.9 % | 7.9 % | ASTM D882 | ||
| Film Elongation at Yield, TD | 6.4 % | 6.4 % | ASTM D882 | ||
| Elmendorf Tear Strength, MD | 3.15 g/micron | 80.0 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 2.625 g/micron | 66.67 g/mil | ASTM D1922 | ||
| Dart Drop | 6.5618 g/micron | 166.67 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 30.5 MPa | 4430 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 27.4 MPa | 3980 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 106 MPa | 15400 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 116 MPa | 16800 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 98.9 °C | 210 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Crystallization Temperature | 85.0 °C | 185 °F | ExxonMobil Method | ||
| Vicat Softening Point | 80.6 °C | 177 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 1.5 % | 1.5 % | ASTM D1003 | ||
| Gloss | 88 % | 88 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.