- 熔體流動速率 [g/10min]: 140.0
- 密度 [g/cm3]: 0.938
- 彎曲模量 [MPa]: 0.0414
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in3 | ExxonMobil Method | ||
| Vinyl Acetate Content | 18.5 % | 18.5 % | ExxonMobil Method | ||
| Melt Flow | 140 g/10 min | 140 g/10 min | 190°C, 2.16 kg; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 82 | 82 | 15s; ASTM D2240 | ||
| Hardness, Shore D | 26 | 26 | 15s; ASTM D2240 | ||
| Tensile Strength at Break | 4.21 MPa | 610 psi | ASTM D638 | ||
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 | ||
| Flexural Modulus | 0.0414 GPa | 6.00 ksi | 1% secant; ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 82.8 °C | 181 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Vicat Softening Point | 47.2 °C | 117 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||