- 熔體流動速率 [g/10min]: 500.0
- 密度 [g/cm3]: 0.933
- 彎曲模量 [MPa]: 0.0372
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.933 g/cc | 0.0337 lb/in3 | ExxonMobil Method |
| Vinyl Acetate Content | 18.7 % | 18.7 % | ExxonMobil Method |
| Melt Flow | 500 g/10 min | 500 g/10 min | 190°C, 2.16 kg; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 75 | 75 | 15s; ASTM D2240 |
| Hardness, Shore D | 23 | 23 | 15s; ASTM D2240 |
| Tensile Strength at Break | 2.90 MPa | 420 psi | ASTM D638 |
| Elongation at Break | 330 % | 330 % | ASTM D638 |
| Flexural Modulus | 0.0372 GPa | 5.40 ksi | 1% secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 77.8 °C | 172 °F | Peak Melting Temperature; ExxonMobil Method |