- 熔體流動速率 [g/10min]: 0.4
- 密度 [g/cm3]: 0.934
- 拉伸強度 [MPa]: 6.31
- 彎曲模量 [MPa]: 0.0876
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.934 g/cc | 0.0337 lb/in3 | ExxonMobil Method |
| Vinyl Acetate Content | 13.3 % | 13.3 % | ExxonMobil Method |
| Melt Flow | 0.40 g/10 min | 0.40 g/10 min | 190 °C, 2.16 kg; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 77 | 77 | 15s; ASTM D2240 |
| Hardness, Shore D | 39 | 39 | 15s; ASTM D2240 |
| Tensile Strength at Break | 15.5 MPa | 2250 psi | ASTM D638 |
| Tensile Strength, Yield | 6.31 MPa | 915 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Elongation at Yield | 180 % | 180 % | ASTM D638 |
| Flexural Modulus | 0.0876 GPa | 12.7 ksi | 1% secant; ASTM D790 |
| Impact Test | 19.0 J | 14.0 ft-lb | Instrument Impact, Total Energy at 23°C; ASTM D3763 |
| 32.5 J | 24.0 ft-lb | Instrument Impact, Total Energy at -40°C; ASTM D3763 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 93.9 °C | 201 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 77.2 °C | 171 °F | ASTM D1525 |