- 密度 [g/cm3]: 1.51
- 吸水率 [%]: 0.3
- 缺口沖擊強(qiáng)度: 9.0
- 彎曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in3 | Crystalline; ISO 1183 | ||
| Water Absorption | 0.30 % | 0.30 % | by immersion; ISO 62-1 | ||
| 0.040 % @Time 86400 sec | 0.040 % @Time 24.0 hour | 3.2 mm thick Tensile bar; ISO 62-1 | |||
| Viscosity | 560000 cP @Temperature 400 °C | 560000 cP @Temperature 752 °F | Melt; ISO 11443 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | 385°C nozzle, 190°C tool; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | 385°C nozzle, 190°C tool; ISO 294-4 | ||
| Spiral Flow | 850 cm @Thickness 1.00 mm | 335 in @Thickness 0.0394 in | 385°C nozzle, 190°C tool; Victrex | ||
| 4100 cm @Thickness 3.00 mm | 1610 in @Thickness 0.118 in | 385°C nozzle, 190°C tool; Victrex | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 89 | 89 | ISO 868 | ||
| Tensile Strength at Break | 35.0 MPa @Temperature 225 °C | 5080 psi @Temperature 437 °F | Result based on 450GL30; ISO 527 | ||
| 60.0 MPa @Temperature 175 °C | 8700 psi @Temperature 347 °F | Result based on 450GL30; ISO 527 | |||
| 120 MPa @Temperature 125 °C | 17400 psi @Temperature 257 °F | Result based on 450GL30; ISO 527 | |||
| 170 MPa @Temperature 23.0 °C | 24700 psi @Temperature 73.4 °F | ISO 527 | |||
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 | ||
| Tensile Modulus | 11.5 GPa | 1670 ksi | ISO 527 | ||
| Flexural Strength | 50.0 MPa @Temperature 225 °C | 7250 psi @Temperature 437 °F | Result based on 450GL30; ISO 178 | ||
| 80.0 MPa @Temperature 175 °C | 11600 psi @Temperature 347 °F | Result based on 450GL30; ISO 178 | |||
| 190 MPa @Temperature 125 °C | 27600 psi @Temperature 257 °F | Result based on 450GL30; ISO 178 | |||
| 260 MPa @Temperature 23.0 °C | 37700 psi @Temperature 73.4 °F | ISO 178 | |||
| Flexural Modulus | 11.0 GPa | 1600 ksi | ISO 178 | ||
| Compressive Strength | 55.0 MPa @Temperature 200 °C | 7980 psi @Temperature 392 °F | Result based on 450GL30; ISO 604 | ||
| 160 MPa @Temperature 120 °C | 23200 psi @Temperature 248 °F | Result based on 450GL30; ISO 604 | |||
| 250 MPa @Temperature 23.0 °C | 36300 psi @Temperature 73.4 °F | Result based on 450GL30; ISO 604 | |||
| Izod Impact, Notched (ISO) | 9.00 kJ/m2 | 4.28 ft-lb/in2 | ISO 180/A | ||
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m2 | 23.8 ft-lb/in2 | ISO 180/U | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 5.00e+15 ohm-cm | 5.00e+15 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.3 @Frequency 1000 Hz | 3.3 @Frequency 1000 Hz | IEC 60093 | ||
| Dielectric Strength | 20.0 kV/mm @Thickness 2.50 mm | 508 kV/in @Thickness 0.0984 in | Result based on 450GL30; IEC 60243-1 | ||
| Dissipation Factor | 0.0050 @Frequency 1.00e+6 Hz | 0.0050 @Frequency 1.00e+6 Hz | Result based on 450GL30; IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 18.0 μm/m-°C | 10.0 μin/in-°F | Along flow below Tg, Result based on 450GL30; ISO 11359 | ||
| 18.0 μm/m-°C | 10.0 μin/in-°F | Along flow above Tg, Result based on 450GL30; ISO 11359 | |||
| CTE, linear, Transverse to Flow | 45.0 μm/m-°C | 25.0 μin/in-°F | Average below Tg, Result based on 450GL30; ISO 11359 | ||
| 110 μm/m-°C | 61.1 μin/in-°F | Average above Tg, Result based on 450GL30; ISO 11359 | |||
| Specific Heat Capacity | 1.70 J/g-°C | 0.406 BTU/lb-°F | DSC | ||
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft2-°F | ISO/CD 22007-4 | ||
| Melting Point | 343 °C | 649 °F | ISO 11357 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 328 °C | 622 °F | ISO 75-f | ||
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 | ||
| UL RTI, Electrical | 240 °C | 464 °F | UL 746B | ||
| UL RTI, Mechanical with Impact | 240 °C | 464 °F | UL 746B | ||
| UL RTI, Mechanical without Impact | 220 °C | 428 °F | UL 746B | ||
| Flammability, UL94 | V-0 @Thickness 0.500 mm | V-0 @Thickness 0.0197 in | |||
| Glow Wire Test | 960 °C @Thickness 2.00 mm | 1760 °F @Thickness 0.0787 in | Result based on 450GL30; IEC 60695-2-12 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 100 °C | <= 212 °F | Hopper Temperature | ||
| Nozzle Temperature | 385 °C | 725 °F | |||
| Zone 1 | 360 °C | 680 °F | |||
| Zone 2 | 370 °C | 698 °F | |||
| Zone 3 | 375 °C | 707 °F | |||
| Zone 4 | 380 °C | 716 °F | |||
| Mold Temperature | 180 - 200 °C | 356 - 392 °F | |||
| <= 250 °C | <= 482 °F | ||||
| Dry Time | 3 hour @Temperature 150 °C | 3 hour @Temperature 302 °F | |||
| 5 hour @Temperature 120 °C | 5 hour @Temperature 248 °F | ||||
| Descriptive Properties | |||||
| Color | Black | ||||
| Gate | > 2mm or 0.5 x part thickness | ||||
| Runner | Die/nozzle > 3mm, manifold > 3.5mm | ||||